Voltage-induced reversible changes in the magnetic coercivity of Fe/ZnO heterostructures

Wen Chin Lin; Po Chun Chang; Cheng Jui Tsai; Tsung Chun Shieh; Fang Yuh Lo

doi:10.1063/1.4865591

Voltage-induced reversible changes in the magnetic coercivity of Fe/ZnO heterostructures

Wen Chin Lin^*
, Po Chun Chang
, Cheng Jui Tsai
, Tsung Chun Shieh
, Fang Yuh Lo

^*此作品的通信作者

物理學系

研究成果: 雜誌貢獻 › 期刊論文 › 同行評審

18 引文斯高帕斯（Scopus）

摘要

In this study, the magnetic coercivity (H_c) of Fe/ZnO heterostructure monotonically decreased as voltage was applied. The reversibility of this effect was demonstrated by cyclically changing the bias voltage from 0 to 6-9 V; the H_c decreased 15%-20%. The H_c value exhibited the same variation whether the applied voltage was positive or negative. As thick Fe-oxide gradually formed at the interface by using direct current heating, the H_c increased and the Fe/ZnO heterostructure demonstrated a similar voltage-induced reduction of H_c.

原文	英語
文章編號	062411
期刊	Applied Physics Letters
卷	104
發行號	6
DOIs	https://doi.org/10.1063/1.4865591
出版狀態	已發佈 - 2014 10月 2

ASJC Scopus subject areas

物理與天文學（雜項）

存取文件

10.1063/1.4865591

其它文件與鏈接

引用此

@article{d94aae9e28434b20af81d11993ab67eb,

title = "Voltage-induced reversible changes in the magnetic coercivity of Fe/ZnO heterostructures",

abstract = "In this study, the magnetic coercivity (Hc) of Fe/ZnO heterostructure monotonically decreased as voltage was applied. The reversibility of this effect was demonstrated by cyclically changing the bias voltage from 0 to 6-9 V; the Hc decreased 15\%-20\%. The Hc value exhibited the same variation whether the applied voltage was positive or negative. As thick Fe-oxide gradually formed at the interface by using direct current heating, the Hc increased and the Fe/ZnO heterostructure demonstrated a similar voltage-induced reduction of Hc.",

author = "Lin, \{Wen Chin\} and Chang, \{Po Chun\} and Tsai, \{Cheng Jui\} and Shieh, \{Tsung Chun\} and Lo, \{Fang Yuh\}",

note = "Publisher Copyright: {\textcopyright} 2014 AIP Publishing LLC.",

year = "2014",

month = oct,

day = "2",

doi = "10.1063/1.4865591",

language = "English",

volume = "104",

journal = "Applied Physics Letters",

issn = "0003-6951",

publisher = "American Institute of Physics Inc.",

number = "6",

}

TY - JOUR

T1 - Voltage-induced reversible changes in the magnetic coercivity of Fe/ZnO heterostructures

AU - Lin, Wen Chin

AU - Chang, Po Chun

AU - Tsai, Cheng Jui

AU - Shieh, Tsung Chun

AU - Lo, Fang Yuh

PY - 2014/10/2

Y1 - 2014/10/2

N2 - In this study, the magnetic coercivity (Hc) of Fe/ZnO heterostructure monotonically decreased as voltage was applied. The reversibility of this effect was demonstrated by cyclically changing the bias voltage from 0 to 6-9 V; the Hc decreased 15%-20%. The Hc value exhibited the same variation whether the applied voltage was positive or negative. As thick Fe-oxide gradually formed at the interface by using direct current heating, the Hc increased and the Fe/ZnO heterostructure demonstrated a similar voltage-induced reduction of Hc.

AB - In this study, the magnetic coercivity (Hc) of Fe/ZnO heterostructure monotonically decreased as voltage was applied. The reversibility of this effect was demonstrated by cyclically changing the bias voltage from 0 to 6-9 V; the Hc decreased 15%-20%. The Hc value exhibited the same variation whether the applied voltage was positive or negative. As thick Fe-oxide gradually formed at the interface by using direct current heating, the Hc increased and the Fe/ZnO heterostructure demonstrated a similar voltage-induced reduction of Hc.

UR - https://www.scopus.com/pages/publications/84921780336

UR - https://www.scopus.com/pages/publications/84921780336#tab=citedBy

U2 - 10.1063/1.4865591

DO - 10.1063/1.4865591

M3 - Article

AN - SCOPUS:84921780336

SN - 0003-6951

VL - 104

JO - Applied Physics Letters

JF - Applied Physics Letters

IS - 6

M1 - 062411

ER -

Voltage-induced reversible changes in the magnetic coercivity of Fe/ZnO heterostructures

摘要

ASJC Scopus subject areas

存取文件

其它文件與鏈接

指紋

引用此