Using anodic aluminum oxide templates and electrochemical method to deposit BiSbTe-based thermoelectric nanowires

Hsin Hui Kuo, Chin Guo Kuo, Chia Ying Yen, Cheng Fu Yang*

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

5 引文 斯高帕斯(Scopus)

摘要

In this study, the cyclic voltammetry method was first used to find the reduced voltages and anodic peaks of Bi3+, Sb3+, and Te4+ ions as the judgments for the growth of the (Bi,Sb)2 - x Te3 + x-based materials. Ethylene glycol (C2H6O2) was used as a solvent, and 0.3 M potassium iodide (KI) was used to improve the conductivity of the solution. Two different electrolyte formulas were first used: (a) 0.01 M Bi(NO3)3-5H2O, 0.01 M SbCl3, and 0.01 M TeCl4 and (b) 0.015 M Bi(NO3)3-5H2O, 0.005 M SbCl3, and 0.0075 M TeCl4. The potentiostatic deposition process was first used to find the effect of reduced voltage on the variation of compositions of the (Bi,Sb)2 - xTe3 + x-based materials. After finding the better reduced voltage, 0.01 M Bi(NO3)3-5H2O, 0.01 M SbCl3, and 0.01 M TeCl4 were used as the electrolyte formula. The pulse deposition process was successfully used to control the composition of the (Bi,Sb)2 - xTe3 + x-based materials and grow the nanowires in anodic aluminum oxide (AAO) templates.

原文英語
文章編號63
頁(從 - 到)1-7
頁數7
期刊Nanoscale Research Letters
9
發行號1
DOIs
出版狀態已發佈 - 2014 12月 1

ASJC Scopus subject areas

  • 一般材料科學
  • 凝聚態物理學

指紋

深入研究「Using anodic aluminum oxide templates and electrochemical method to deposit BiSbTe-based thermoelectric nanowires」主題。共同形成了獨特的指紋。

引用此