The Annealing Effect at Different Temperatures for Organic-Inorganic Perovskite Quantum Dots

Shui Yang Lien, Pin Jia Lai, Wen Ray Chen, Chuan Hsi Liu, Po Wen Sze, Chien Jung Huang*

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

3 引文 斯高帕斯(Scopus)

摘要

After the preparation of inorganic perovskite cesium lead iodide quantum dots (CsPbI3 QD) by ligand-assisted reprecipitation (LARP), CsPbI3 QD was added to the organic perovskite methylamine lead triiodide (CH3 NH3 PbI3; MAPbI3) to successfully form composite perovskite film. To obtain better perovskite quantum dot (PQD) crystal characteristics, this research used different annealing temperatures to discuss the crystallinity changes of perovskite quantum dots (PQD). Through X-ray diffraction (XRD) analysis, it was found that the preferred peak (110) of MAPbI3 had maximum peak intensity when the annealing temperature increased to 120 C. Based on the measurement results of PQD’s Ultraviolet-Visible spectrum, it was shown that the maximum absorption area was obtained at the wavelength of 350 nm~750 nm at the annealing temperature 120 C. From the scanning electron microscope (SEM) measurement, it was found that the grain size was the largest at the annealing temperature 120 C, and the grain size was 60.2 nm. The best crystallization characteristics of PQD were obtained at the annealing temperature 120 C.

原文英語
文章編號204
期刊Crystals
12
發行號2
DOIs
出版狀態已發佈 - 2022 2月

ASJC Scopus subject areas

  • 一般化學工程
  • 一般材料科學
  • 凝聚態物理學
  • 無機化學

指紋

深入研究「The Annealing Effect at Different Temperatures for Organic-Inorganic Perovskite Quantum Dots」主題。共同形成了獨特的指紋。

引用此