Surface modification of Ni-YSZ using niobium oxide for sulfur-tolerant anodes in solid oxide fuel cells

Songho Choi, Jenghan Wang, Zhe Cheng, Meilin Liu

    研究成果: 雜誌貢獻文章同行評審

    45 引文 斯高帕斯(Scopus)

    摘要

    The surface of a dense Ni-yttria-stabilized zirconia (YSZ) anode for solid oxide fuel cells (SOFCs) was modified with niobium oxide (Nb2 O5) in order to achieve sulfur tolerance. Results suggest that Nb2 O5 was reduced to NbO2 under SOFC operating conditions, which has high electrical conductivity and catalytic activity toward hydrogen oxidation. The NbOx -coated dense Ni-YSZ cermet anode showed sulfur tolerance when exposed to 50 ppm H2 S at 700°C over 12 h. Raman spectroscopy and X-ray diffraction analysis suggest that different phases of niobium sulfides (NbSx) were formed on the surfaces of niobium oxides. Furthermore, density of state (DOS) analysis of NbO2, NbS, and NbS2 indicates that the electronic structure of niobium sulfides are similar to that of NbO2; they are electrically conductive and catalytically active for hydrogen oxidation in H2 S containing fuels under the conditions studied.

    原文英語
    頁(從 - 到)B449-B454
    期刊Journal of the Electrochemical Society
    155
    發行號5
    DOIs
    出版狀態已發佈 - 2008 四月 15

    ASJC Scopus subject areas

    • Electronic, Optical and Magnetic Materials
    • Renewable Energy, Sustainability and the Environment
    • Surfaces, Coatings and Films
    • Electrochemistry
    • Materials Chemistry

    指紋 深入研究「Surface modification of Ni-YSZ using niobium oxide for sulfur-tolerant anodes in solid oxide fuel cells」主題。共同形成了獨特的指紋。

    引用此