Superconductivity at 124 K in (Tl, Pb)Sr2Ca2Cu3O9

R. S. Liu, Shu-Fen Hu, D. A. Jefferson, P. P. Edwards

研究成果: 雜誌貢獻期刊論文同行評審

33 引文 斯高帕斯(Scopus)

摘要

We report the preparation of almost phase pure (Tl0.5Pb0.5)Sr2Ca2Cu3O9, which is characterized by high temperature superconduc tivity with Tc onset=130 K, Tc midpoint=124 K, Tc zero=122.5 K as measured by electrical resistance, and a diamagnetic onset temperature, Tc mag of 124 K determined by DC magnetic susceptibility. The new procedure involves synthesizing a material with nominal stoichiometry (Tl0.5Pb0.5)Sr1.6Ca2.4Cu3O9, which is encapsulated in gold foil and sintered at 950°C for 3 h in oxyge n, then sealed in an evacuated quartz tube and finally annealed at 700∼750°C for 5∼10 days. From the results of X-ray diffraction and energy-dispersive X-ray spectrometry (EDS), we have identified the phase responsible for the superconductivity in the annealed sample to be Tl0.58(3)Pb0.38(2)Sr1.9(2)Ca2.1(1)Cu3O9 . No superlattice and intergrowth along the a* and c* directions were observed but streaks along the c*-axis were found from microcrystallites of the annealed sample.

原文英語
頁(從 - 到)318-322
頁數5
期刊Physica C: Superconductivity and its applications
198
發行號3-4
DOIs
出版狀態已發佈 - 1992 八月 1

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

指紋 深入研究「Superconductivity at 124 K in (Tl, Pb)Sr<sub>2</sub>Ca<sub>2</sub>Cu<sub>3</sub>O<sub>9</sub>」主題。共同形成了獨特的指紋。

引用此