Study on Pt(Sn)/TiO2-C as Anodic Catalysts for Direct Ethanol Fuel Cell

Chiu Hung Liu, Mao Huang Liu, Ying Huei Liu, Chia Jung Lu, Chia Chih Chang, Chih Chia Wang, Chen Bin Wang

研究成果: 雜誌貢獻期刊論文同行評審

摘要

This research concentrated on the use of a modified Pt/C anodic catalyst with titania (TiO2) and tin (Sn) to enhance the utilization and efficiency of a direct ethanol fuel cell. The TiO2-doped active carbon support (TiO2-C) was prepared by the impregnation method. Then, using platinum chloride (PtCl4) and tin (II) chloride dihydrate (SnCl2.2H2O) as precursors, a Pt(Sn)/TiO2-C anodic catalyst was fabricated by the formic acid reduction method. Further, a series of Pt(Sn)/TiO2-C anodic catalysts were coated on carbon paper as working electrodes. Performance evaluations were executed by cyclic voltammetry (CV) and chronoamperometry for the ethanol electro-oxidation, and CO stripping voltammetry was performed in an acid solution at room temperature. Characterization of the series Pt(Sn)/TiO2-C catalysts displayed that all catalysts revealed uniform dispersion of platinum with a diameter around 3 - 6 nm and a high electrochemically active surface area. Apparently, the doping of TiO2 and Sn could disperse the active species, and lower the potential of the ethanol electro-oxidation to improve the ethanol oxidation reaction (EOR). In addition, the inclusion of TiO2 and Sn could promote CO stripping by the surface active OHad sites and through the formation of a PtSn2 alloy at a lower oxidizing potential.

原文英語
頁(從 - 到)12395-12409
頁數15
期刊International Journal of Electrochemical Science
15
DOIs
出版狀態已發佈 - 2020

ASJC Scopus subject areas

  • 電化學

指紋

深入研究「Study on Pt(Sn)/TiO<sub>2</sub>-C as Anodic Catalysts for Direct Ethanol Fuel Cell」主題。共同形成了獨特的指紋。

引用此