Studies of longitudinal and transverse resistivities of YBa2Cu3Oy/R0.7M0.3MnO 3 superlattices, in which R = La or Nd and M = Ca or Sr

J. C. Chen*, H. C. Yang, L. M. Wang, H. E. Horng

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

摘要

We measured the longitudinal and transverse Hall resistivities of YBa2Cu3Oy/R1-xMxMnO3 superlattices in magnetic fields to study the transport properties, in which R = La or Nd and M = Ca or Sr. The resistive transition in the magnetic field shows a thermally activated flux flow behaviour. The flux pinning ability of the superlattice is reduced when the coupling strength between YBa2Cu3Oy layers is decreased. The transverse Hall resistivity shows sign reversal for samples with strong pinning ability. The sign reversal diminishes as the pinning force is reduced. The magnetoresistance (MR) ratio, |Δρ(H) - Δρ(H = 0)|/Δρ(H), of the YBa2Cu3Oy/R1-xMxMnO3 superlattice is affected by the coupling strength of R1-xMxMnO3 layers. The peak values of the MR ratio were shifted to lower temperatures in superlattices due to the lowering of the magnetic ordering in ferromagnetic layers.

原文英語
頁(從 - 到)1011-1016
頁數6
期刊Superconductor Science and Technology
15
發行號7
DOIs
出版狀態已發佈 - 2002 7月

ASJC Scopus subject areas

  • 陶瓷和複合材料
  • 凝聚態物理學
  • 金屬和合金
  • 電氣與電子工程
  • 材料化學

指紋

深入研究「Studies of longitudinal and transverse resistivities of YBa2Cu3Oy/R0.7M0.3MnO 3 superlattices, in which R = La or Nd and M = Ca or Sr」主題。共同形成了獨特的指紋。

引用此