Studies of longitudinal and transverse resistivities of YBa2Cu3Oy/R0.7M0.3MnO 3 superlattices, in which R = La or Nd and M = Ca or Sr

J. C. Chen, H. C. Yang, L. M. Wang, H. E. Horng

    研究成果: 雜誌貢獻期刊論文同行評審


    We measured the longitudinal and transverse Hall resistivities of YBa2Cu3Oy/R1-xMxMnO3 superlattices in magnetic fields to study the transport properties, in which R = La or Nd and M = Ca or Sr. The resistive transition in the magnetic field shows a thermally activated flux flow behaviour. The flux pinning ability of the superlattice is reduced when the coupling strength between YBa2Cu3Oy layers is decreased. The transverse Hall resistivity shows sign reversal for samples with strong pinning ability. The sign reversal diminishes as the pinning force is reduced. The magnetoresistance (MR) ratio, |Δρ(H) - Δρ(H = 0)|/Δρ(H), of the YBa2Cu3Oy/R1-xMxMnO3 superlattice is affected by the coupling strength of R1-xMxMnO3 layers. The peak values of the MR ratio were shifted to lower temperatures in superlattices due to the lowering of the magnetic ordering in ferromagnetic layers.

    頁(從 - 到)1011-1016
    期刊Superconductor Science and Technology
    出版狀態已發佈 - 2002 七月

    ASJC Scopus subject areas

    • Ceramics and Composites
    • Condensed Matter Physics
    • Metals and Alloys
    • Electrical and Electronic Engineering
    • Materials Chemistry

    指紋 深入研究「Studies of longitudinal and transverse resistivities of YBa<sub>2</sub>Cu<sub>3</sub>O<sub>y</sub>/R<sub>0.7</sub>M<sub>0.3</sub>MnO <sub>3</sub> superlattices, in which R = La or Nd and M = Ca or Sr」主題。共同形成了獨特的指紋。