Structural, optical, and magnetic properties of Ho-implanted GaN thin films

F. Y. Lo, J. Y. Guo, V. Ney, A. Ney, M. Y. Chern, A. Melnikov, S. Pezzagna, D. Reuter, A. D. Wieck, J. Massies

研究成果: 雜誌貢獻期刊論文同行評審

1 引文 斯高帕斯(Scopus)

摘要

Ho ions were implanted into highly-resistive molecular-beam-epitaxy grown GaN thin films with a 100kV focused-ion-beam implanter at room temperature (RT). The implantation doses of Ho ions ranges from 1014 to 10 16 cm-2. Without thermal annealing, the structural, optical, and magnetic properties of the Ho-implanted thin films were investigated. Structural properties studied by x-ray diffraction revealed Ho incorporation into GaN matrix without secondary phase. The overall photoluminescence of any implanted sample is weaker than that of the non-implanted one. The spectra show neutral-donor-bound exciton emission and defect-related blue luminescence. Blocked superparamagnetic behavior was identified from Ho-implanted samples at temperatures below RT by measurements with a superconducting quantum interference device. The highest ordering temperature is 100 K.

原文英語
文章編號012097
期刊Journal of Physics: Conference Series
266
發行號1
DOIs
出版狀態已發佈 - 2011 一月 1

ASJC Scopus subject areas

  • 物理與天文學 (全部)

指紋

深入研究「Structural, optical, and magnetic properties of Ho-implanted GaN thin films」主題。共同形成了獨特的指紋。

引用此