Signature of lattice defects in far infrared reflectivity of Ba(Mg1/3Ta2/3)O3

T. Shimada, K. Touji, Hsiang Lin Liu, Yuan Tai Tzeng, Chi-Ta Chia, T. Kolodiazhnyi

研究成果: 雜誌貢獻文章

6 引文 斯高帕斯(Scopus)

摘要

Far infrared reflectivity spectra of Ba(Mg1/3,Ta2/3)O3 prepared at several sintering temperatures were measured, and the eigenfrequencies and damping constants of the TO modes were determined. The reflectivity spectra were fitted with the four-parameter semi-quantum model. The variation in the Eu(OII) at 222 cm-1 and A2u(OII) at 238 cm-1 modes in well ordered ceramics was attributed to the variation in the concentration of the B site defects. It was also found that the change in the oxygen partial pressure of the sintering atmosphere causes a change in the seventh (316 cm-1) and eighth (352 cm-1) modes. We attribute these changes to the oxygen site defect although we cannot evaluate the concentration of this defect at this moment. From the behavior of the damping constants it is suggested that the Ba(Mg1/3Ta2/3)O3 (BMT) attains equilibrium defect density at the heat treatment temperature of more than 1630 °C (120 h).

原文英語
頁(從 - 到)2797-2802
頁數6
期刊Journal of the European Ceramic Society
27
發行號8-9 SPEC. ISS.
DOIs
出版狀態已發佈 - 2007 四月 2

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

指紋 深入研究「Signature of lattice defects in far infrared reflectivity of Ba(Mg<sub>1/3</sub>Ta<sub>2/3</sub>)O<sub>3</sub>」主題。共同形成了獨特的指紋。

  • 引用此