Reversible 90-Degree Rotation of Fe Magnetic Moment Using Hydrogen

Chuan Che Hsu, Po Chun Chang, Yi Hua Chen, Chak Ming Liu, Chun Te Wu, Hung Wei Yen, Wen Chin Lin*


研究成果: 雜誌貢獻期刊論文同行評審

9 引文 斯高帕斯(Scopus)


[Pd/Fe]2 multilayers were deposited on a flat MgO(001) to study the effect of hydrogen on magnetic interlayer coupling. Complex magnetic hysteresis behavior, including single, double, and triple loops, were measured as a function of the azimuthal angle in a longitudinal and transverse direction. With a combination of a 2-fold magnetic anisotropy energy (MAE) in the bottom-Fe and a 4-fold MAE in the top-Fe, the complex magnetic hysteresis behavior could be clearly explained. Two well-split hysteresis loops with almost zero Kerr remanence were measured by choosing a suitable Pd thickness and applying the magnetic field perpendicular to the easy axis of the bottom-Fe. The split double loops originated from the 90°-rotation of the top-Fe moment. On exposure to a hydrogen gas atmosphere, the separation of the two minor loops increased, indicating that Pd-hydride formation enhanced the ferromagnetic coupling between the two Fe layers. Based on these observations, we proposed that, by applying a suitable constant magnetic field, the top-Fe moment could undergo reversible 90°-rotation following hydrogen exposure. The results suggest that the Pd space layer used for mediating the magnetic interlayer coupling is sensitive to hydrogen, and therefore, the multilayer system can function as a giant magnetoresistance-type sensor suitable for hydrogen gas.

期刊Scientific reports
出版狀態已發佈 - 2018 12月 1

ASJC Scopus subject areas

  • 多學科


深入研究「Reversible 90-Degree Rotation of Fe Magnetic Moment Using Hydrogen」主題。共同形成了獨特的指紋。