Raman spectra and extended X-ray absorption fine structure characterization of La(2-x)/3NaxTiO3 and Nd(2-x)/3LixTiO3 microwave ceramics

Mei Yu Chen, Ching Yu Chiu, Chia Ta Chia, J. F. Lee, J. J. Bian

研究成果: 雜誌貢獻期刊論文同行評審

8 引文 斯高帕斯(Scopus)

摘要

A-site deficient perovskite compounds, La(2-x)/3NaxTiO3 (0.02 ≤ x ≤ 0.5) and Nd(2-x)/3LixTiO3 (0.1 ≤ x ≤ 0.5) microwave ceramics, were investigated by Raman scattering. Nd(2-x)/3LixTiO3 (0.1 ≤ x ≤ 0.5) was also investigated by extended X-ray absorption fine structure (EXAFS) measurement. The Raman shifts of the E (239 cm-1) and A1 (322 cm-1) modes of La(2-x)/3NaxTiO3 were found to decrease with x. However, the E (254 cm-1) and A1 (338 cm-1) of Nd(2-x)/3LixTiO3 were found to blueshift with x, which was caused by Li substitution. The redshift of the A1 (471 cm-1) phonon of Nd(2-x)/3LixTiO3 (0.1 ≤ x ≤ 0.3) indicates that O-Ti-O bonding forces lessen with Li concentration, which is consistent with the EXAFS result that Ti-O bond lengths increase for 0.1 ≤ x ≤ 0.3. For x > 0.3, the EXAFS result shows that Ti-O bond lengths decrease. Moreover, Ti-O bond lengths show strong correlation with the microwave dielectric constants of Nd(2-x)/3LixTiO3.

原文英語
頁(從 - 到)335-339
頁數5
期刊Journal of the European Ceramic Society
30
發行號2
DOIs
出版狀態已發佈 - 2010 一月

ASJC Scopus subject areas

  • Ceramics and Composites
  • Materials Chemistry

指紋 深入研究「Raman spectra and extended X-ray absorption fine structure characterization of La<sub>(2-x)/3</sub>Na<sub>x</sub>TiO<sub>3</sub> and Nd<sub>(2-x)/3</sub>Li<sub>x</sub>TiO<sub>3</sub> microwave ceramics」主題。共同形成了獨特的指紋。

引用此