Promoted activity of annealed Rh nanoclusters on thin films of Al2O3/NiAl(100) in the dehydrogenation of Methanol-d4

Ting Chieh Hung, Ting Wei Liao, Guan Jr Liao, Zhen He Liao, Po Wei Hsu, Yu Ling Lai, Yao Jane Hsu, Chia Hsin Wang, Yaw Wen Yang, Jeng Han Wang, Meng Fan Luo*

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

摘要

Annealed Rh nanoclusters on an ordered thin film of Al2O3/NiAl(100) were shown to exhibit a promoted reactivity toward the decomposition of methanol-d4, under both ultrahigh vacuum and near-ambient-pressure conditions. The Rh clusters were grown with vapor deposition onto the Al2O3/NiAl(100) surface at 300 K and annealed to 700 K. The decomposition of methanol-d4proceeded only through dehydrogenation, with CO and deuterium as products, on Rh clusters both as prepared and annealed. Nevertheless, the catalytic reactivity of the annealed clusters, measured with the production of either CO or deuterium per surface Rh site from the reaction, became at least 2-3 times that of the as-prepared ones. The promoted reactivity results from an altered support effect associated with an annealing-induced mass transport at the surface. Our results demonstrate a possibility to practically prepare reactive Rh clusters, regardless of the cluster size, that can tolerate an elevated reaction temperature, with no decreased reactivity.

原文英語
頁(從 - 到)24762-24771
頁數10
期刊RSC Advances
11
發行號40
DOIs
出版狀態已發佈 - 2021 七月 12

ASJC Scopus subject areas

  • 化學 (全部)
  • 化學工程 (全部)

指紋

深入研究「Promoted activity of annealed Rh nanoclusters on thin films of Al<sub>2</sub>O<sub>3</sub>/NiAl(100) in the dehydrogenation of Methanol-d<sub>4</sub>」主題。共同形成了獨特的指紋。

引用此