p-type α-Fe2O3 nanowires and their n-type transition in a reductive ambient

Yu Chen Lee, Yu Lun Chueh, Chin Hua Hsieh, Mu Tung Chang, Li Jen Chou, Zhong Lin Wang, Yann Wen Lan, Chii Dong Chen, Hiroki Kurata, Seiji Isoda

研究成果: 雜誌貢獻文章

96 引文 斯高帕斯(Scopus)

摘要

The synthesis and electronic properties of p-type Α-Fe 2O3 nanowires and their n-type transition in a reductive ambient with ordered oxygen vacancies were analyzed. Α-Fe 2O3 was the most stable iron oxide compound material, widely used in photoelectrodes, gas sensing, catalysts, magnetic recording, and in medical fields. SEM and image of Α-Fe2O3 nanowires synthesized on an Fe64Ni36 substrate at 450°C for 10 hours in an Ar ambient of 100 seem was done. A typical TEM image of nanowire with diameter of 18nm was analyzed. The corresponding diffraction pattern confirms the phase of Α-Fe2O3 with a [001] zone axis. The results show that p-type nature of iron oxide nanowire were mainly caused by strong surface adsorption owing to the oxygen vacancies and the large surface to volume ratio.

原文英語
頁(從 - 到)1356-1361
頁數6
期刊Small
3
發行號8
DOIs
出版狀態已發佈 - 2007 八月

ASJC Scopus subject areas

  • Biotechnology
  • Biomaterials
  • Chemistry(all)
  • Materials Science(all)

指紋 深入研究「p-type α-Fe<sub>2</sub>O<sub>3</sub> nanowires and their n-type transition in a reductive ambient」主題。共同形成了獨特的指紋。

引用此