Optical properties of Na0.68CoO2 thin film

M. H. Hsu*, H. L. Liu, W. J. Chang, J. Y. Lin

*此作品的通信作者

研究成果: 雜誌貢獻會議論文同行評審

摘要

The optical reflectance of single-crystalline Na0.68CoO 2 (thickness around 3000 Å) thin film has been measured over a wide frequency (40-55000 cm-1) and at temperatures between 20 and 300 K. The roomtemperature optical conductivity spectrum displays a metallic character. In addition, one E1u phonon mode at about 518 cm -1 is identified, while the other four phonon peaks are due to the sapphire substrate. As the temperature is lowered, the Drude plasma frequency exhibits little temperature dependence, whereas the scattering rate monotonically decreases with decreasing temperature. Notably, the Drude scattering rate at 20 K is found to approach zero, consistent with the small residual resistivity, indicating high quality of Na0.68CoO 2 thin film.

原文英語
頁(從 - 到)4483-4486
頁數4
期刊Physica Status Solidi (C) Current Topics in Solid State Physics
4
發行號12
DOIs
出版狀態已發佈 - 2007
事件International Symposium on Advanced Magnetic Materials and Appilications, (ISAMMA 2007) - Jeju, 大韓民國
持續時間: 2007 五月 282007 六月 1

ASJC Scopus subject areas

  • 凝聚態物理學

指紋

深入研究「Optical properties of Na<sub>0.68</sub>CoO<sub>2</sub> thin film」主題。共同形成了獨特的指紋。

引用此