Nanoparticles of Pb-Bi eutectic nucleation and growth on alumina template

Chien Chon Chen*, Chin Guo Kuo, Jung Hsuan Chen, Chuen Guang Chao


研究成果: 雜誌貢獻期刊論文同行評審

11 引文 斯高帕斯(Scopus)


A novel and convenient method of thermo-immersion was used to fabricate of a large of lead-bismuth (Pb-Bi) eutectic nanoparticles on an uniform size anodic aluminum oxide (AAO) template. The AAO with a 60 nm pore diameter was used as a template for nanoparticles nucleation and growth. Both Pb-Bi and AAO were placed in a glass tube in vacuum at 10-6 Torr, controlled by a molecular turbo pump then heated up to the melting point of the alloy. Nanoparticles nucleated and grew on the AAO template when the molten Pb-Bi solidified. The nanoparticles nucleated on the pore corners of the AAO template initially, grew simultaneously and assembled into a big nanoparticle on top of the AAO template later. Additionally, the size diameters of the initial nanoparticles were approximately 15 nm on the pore corners of the AAO template, and 80 nm when the initial nanoparticles formed a large nanoparticle. Latent heat was released when the molten Pb-Bi solidified to form nanoparticles. The size diameters distribution of nanoparticles was observed by scanning electron microscopy (SEM) such that, the diameters of the nanoparticles were 80 nm on top of the AAO template, and 200 nm in depths of the concave.

頁(從 - 到)8354-8359
期刊Japanese Journal of Applied Physics, Part 1: Regular Papers and Short Notes and Review Papers
出版狀態已發佈 - 2004 12月

ASJC Scopus subject areas

  • 工程 (全部)
  • 物理與天文學 (全部)


深入研究「Nanoparticles of Pb-Bi eutectic nucleation and growth on alumina template」主題。共同形成了獨特的指紋。