Multipolar Resonances of Ag Nanoparticle Arrays in Anodic Aluminum Oxide Nanochannels for Enhanced Hot Spot Intensity and Signal-to-Background Ratio in Surface-Enhanced Raman Scattering

Hui Hsin Hsiao*, Hao Ke, Mykhaylo M. Dvoynenko, Juen Kai Wang

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

1 引文 斯高帕斯(Scopus)

摘要

Hot spots generated through the electrodynamic coupling of the local plasmons in metallic nanoparticles play an important role in enhancing surface-enhanced Raman spectroscopy (SERS) signal. However, the accompanied increasing penetration field inside the nanoparticles is known to be one of the mechanisms contributing to the continuum background. Here, we systematically explored the multipolar resonances for SERS substrates comprised of Ag-nanoparticle (Ag-NP) arrays grown in anodic aluminum oxide nanochannels and their roles in affecting the signal amplification and the background noise at three typical wavelengths for Raman spectroscopy (532, 633, and 785 nm). By varying the diameters of the Ag-NP arrays, different orders of electric-quadrupole (EQ) modes are excited at each studied wavelength. Compared to the dipolar resonance, the second-order EQ mode was found to exhibit stronger hot spot intensity confined at the exposed side of the nanogaps, which are beneficial to serve as active sites interacting with analyte molecules. More importantly, a significant suppressed SERS background was achieved for these higher-order modes due to their small penetration depth inside the particles. The enhanced signal-to-background ratio for the second EQ mode was validated among the three Raman wavelengths, which provide promising design guideline for SERS-active substrates with higher sensitivity.

原文英語
頁(從 - 到)4477-4485
頁數9
期刊ACS Applied Nano Materials
3
發行號5
DOIs
出版狀態已發佈 - 2020 五月 22

ASJC Scopus subject areas

  • 材料科學(全部)

指紋

深入研究「Multipolar Resonances of Ag Nanoparticle Arrays in Anodic Aluminum Oxide Nanochannels for Enhanced Hot Spot Intensity and Signal-to-Background Ratio in Surface-Enhanced Raman Scattering」主題。共同形成了獨特的指紋。

引用此