Multi-layer organic light-emitting diodes processed from solution using phosphorescent dendrimers in a polymer host

Li Chun Ko, Tsung Yu Liu, Chun Yao Chen, Chung Ling Yeh, Shin Rong Tseng, Yu Chiang Chao, Hsin Fei Meng*, Shih Chun Lo, Paul L. Burn, Sheng Fu Horng

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

23 引文 斯高帕斯(Scopus)

摘要

A uniform dispersion of highly soluble phosphorescent dendrimer emitters is achievedby blending with a polymer host poly(9-vinylcarbazole) (PVK) containing N,N′-diphenyl-N, N′-(bis(3-methylphenyl)-[1,1-biphenyl]-4,4′- diamine (TPD) and 2-(4-biphen-4′-yl)-5-(4- tert-butylphenyl)-1,3,4- oxadiazole (PBD). No visible aggregation orself-quenching was observed for guest-to-host weight ratios of up to 33:67. The dendrimers contain a factris( 2-phenylpyridyl)iridium(III) [Ir(ppy)3] core, first generation biphenyl-based dendrons, and 2-ethylhexyloxy surface groups. The guest-host blend is used for all solution processed organic light-emitting diodes. A maximum external and current efficiency of 10.2% and 38 cd/A (at 5 V and a brightness of 50 cd/m2), and a maximum brightness of 27,000 cd/m 2 (at 14.5 V), were obtained when a CsF/Al cathode was used. Blade coating was used to fabricate a multi-layer structure that also contained an electron-transport layer. The device that had a LiF/Al cathode had a maximal efficiency of 40 cd/A corresponding to an external quantum efficiency of 10.8% (at 5 V and a brightness of 19 cd/m2). The maximum brightness of the second device was 17,840 cd/m2 at 14 V.

原文英語
頁(從 - 到)1005-1009
頁數5
期刊Organic Electronics
11
發行號6
DOIs
出版狀態已發佈 - 2010 六月

ASJC Scopus subject areas

  • 電子、光磁材料
  • 生物材料
  • 化學 (全部)
  • 凝聚態物理學
  • 材料化學
  • 電氣與電子工程

指紋

深入研究「Multi-layer organic light-emitting diodes processed from solution using phosphorescent dendrimers in a polymer host」主題。共同形成了獨特的指紋。

引用此