Magnetoresistance of la0.7 Sr0.3 MnO3 film at room temperature

S. Y. Yang, W. L. Kuang, C. H. Ho, W. S. Tse, M. T. Lin, S. F. Lee, Y. Liou, Y. D. Yao

研究成果: 雜誌貢獻期刊論文同行評審

16 引文 斯高帕斯(Scopus)

摘要

The La0.7 Sr0.3MnO3 (LSMO) film is deposited successfully onto a MgO (001) substrate by using a magnetron DC sputtering system. The θ-20 X-ray diffraction pattern is detected to investigate the structure of the deposited LSMO film. According to the experimental temperature dependent magnetization result, the Curie temperature of the sample is 364.8 K. The magnetic hysteresis curve with a coercivity of 17 Oe was found for the LSMO film at 300K, meanwhile, a significant magnetoresistance was observed. With these properties at room temperature, the LSMO-based devices might be very suitable for practical applications.

原文英語
頁(從 - 到)690-692
頁數3
期刊Journal of Magnetism and Magnetic Materials
226-230
發行號PART I
DOIs
出版狀態已發佈 - 2001
對外發佈

ASJC Scopus subject areas

  • 電子、光磁材料
  • 凝聚態物理學

指紋

深入研究「Magnetoresistance of la<sub>0.7</sub> Sr<sub>0.3</sub> MnO<sub>3</sub> film at room temperature」主題。共同形成了獨特的指紋。

引用此