Magnetic property enhancement of cobalt-free M-type strontium hexagonal ferrites by CaCO3 and SiO2 addition

Ching Chien Huang, Ai Hua Jiang, Ching Hsuan Liou, Yi Chen Wang, Chi Ping Lee, Tong Yin Hung, Chun Chung Shaw, Yung Hsiung Hung, Ming Feng Kuo, Chun Hu Cheng

研究成果: 雜誌貢獻期刊論文同行評審

9 引文 斯高帕斯(Scopus)

摘要

An experiment was performed to investigate whether CaCO3 and SiO2 addition enhances the magnetic properties of cobalt-free M-type Sr ferrites, in which experimental parameters such as additive composition and the CaCO3/SiO2 ratio were changed. The specimens were prepared using conventional ceramic techniques. CaCO3 addition promoted densification and uniform grain growth, resulting in high remanence; however, with the simultaneous addition of CaCO3 and SiO2, coercivity decreased to 3046 Oe in Sr ferrite hard magnets without Co3O4. SiO2 addition suppressed grain growth. The addition of appropriate concentrations of CaCO3 and SiO2 as additives after calcination was shown to be very beneficial for tailoring a dense microstructure with relatively small grains. A CaCO3/SiO2 ratio of approximately 1.8 was found to be optimum, and the magnetic properties of Br = 4.3 kG, iHc = 3.7 kOe, and (BH)max = 4.5 MGOe were obtained for Sr ferrite hard magnets without Co3O4, which are acceptable for motor applications under output power <1 kW.

原文英語
頁(從 - 到)111-117
頁數7
期刊Intermetallics
89
DOIs
出版狀態已發佈 - 2017 十月

ASJC Scopus subject areas

  • 化學 (全部)
  • 材料力學
  • 機械工業
  • 金屬和合金
  • 材料化學

指紋

深入研究「Magnetic property enhancement of cobalt-free M-type strontium hexagonal ferrites by CaCO<sub>3</sub> and SiO<sub>2</sub> addition」主題。共同形成了獨特的指紋。

引用此