Magnetic properties of high-oxygen pressure prepared PrBa2Cu3O7-y cuprates

Y. H. Lin; B. N. Lin; Y. X. Lin; Y. Y. Hsu; T. I. Hsu; H. C. Ku

doi:10.1063/1.1357859

Magnetic properties of high-oxygen pressure prepared PrBa₂Cu₃O_7-y cuprates

Y. H. Lin^*, B. N. Lin, Y. X. Lin, Y. Y. Hsu, T. I. Hsu, H. C. Ku

^*此作品的通信作者

研究成果: 雜誌貢獻 › 會議論文 › 同行評審

摘要

High oxygen pressure annealed PrBa₂Cu₃O_7-y (y∼0) cuprates were prepared in order to study the effect of oxygen stoichiometric parameter y on the unusual Pr/Cu magnetic properties and/or recently reported superconductivity. The oxygen-rich orthorhombic 123-chain phase is highly unstable under high-oxygen pressure synthesis and decomposes completely in 10 bar pressure. For a smaller 2 bar prepared sample a relatively clean phase was preserved with an oxygen parameter y = 0.05, as compared with y = 0.11 from a conventional 1 bar flowing oxygen method. No superconductivity can be detected for all high-oxygen pressure prepared samples. Instead, Mott-insulator behavior with anomalous high Pr ordering T_N(Pr) = 19 K was observed for PrBa₂Cu₃O_6.95. Comparison with other Pr/Ba intersubstituted Pr_1-xBa_2-xCu₃O_7-y cuprates is discussed.

原文	英語
頁（從 - 到）	7484-7486
頁數	3
期刊	Journal of Applied Physics
卷	89
發行號	11 II
DOIs	https://doi.org/10.1063/1.1357859
出版狀態	已發佈 - 2001 6月 1
對外發佈	是
事件	8th Joint Magnetism and Magnetic Materials-Intermag Conference - San Antonio, TX, 美国持續時間: 2001 1月 7 → 2001 1月 11

ASJC Scopus subject areas

一般物理與天文學

存取文件

10.1063/1.1357859

其它文件與鏈接

引用此

@article{271af2176ff640a9a0739ce1f204b309,

title = "Magnetic properties of high-oxygen pressure prepared PrBa2Cu3O7-y cuprates",

abstract = "High oxygen pressure annealed PrBa2Cu3O7-y (y∼0) cuprates were prepared in order to study the effect of oxygen stoichiometric parameter y on the unusual Pr/Cu magnetic properties and/or recently reported superconductivity. The oxygen-rich orthorhombic 123-chain phase is highly unstable under high-oxygen pressure synthesis and decomposes completely in 10 bar pressure. For a smaller 2 bar prepared sample a relatively clean phase was preserved with an oxygen parameter y = 0.05, as compared with y = 0.11 from a conventional 1 bar flowing oxygen method. No superconductivity can be detected for all high-oxygen pressure prepared samples. Instead, Mott-insulator behavior with anomalous high Pr ordering TN(Pr) = 19 K was observed for PrBa2Cu3O6.95. Comparison with other Pr/Ba intersubstituted Pr1-xBa2-xCu3O7-y cuprates is discussed.",

author = "Lin, {Y. H.} and Lin, {B. N.} and Lin, {Y. X.} and Hsu, {Y. Y.} and Hsu, {T. I.} and Ku, {H. C.}",

year = "2001",

month = jun,

day = "1",

doi = "10.1063/1.1357859",

language = "English",

volume = "89",

pages = "7484--7486",

journal = "Journal of Applied Physics",

issn = "0021-8979",

publisher = "American Institute of Physics Publising LLC",

number = "11 II",

note = "8th Joint Magnetism and Magnetic Materials-Intermag Conference ; Conference date: 07-01-2001 Through 11-01-2001",

}

TY - JOUR

T1 - Magnetic properties of high-oxygen pressure prepared PrBa2Cu3O7-y cuprates

AU - Lin, Y. H.

AU - Lin, B. N.

AU - Lin, Y. X.

AU - Hsu, Y. Y.

AU - Hsu, T. I.

AU - Ku, H. C.

PY - 2001/6/1

Y1 - 2001/6/1

N2 - High oxygen pressure annealed PrBa2Cu3O7-y (y∼0) cuprates were prepared in order to study the effect of oxygen stoichiometric parameter y on the unusual Pr/Cu magnetic properties and/or recently reported superconductivity. The oxygen-rich orthorhombic 123-chain phase is highly unstable under high-oxygen pressure synthesis and decomposes completely in 10 bar pressure. For a smaller 2 bar prepared sample a relatively clean phase was preserved with an oxygen parameter y = 0.05, as compared with y = 0.11 from a conventional 1 bar flowing oxygen method. No superconductivity can be detected for all high-oxygen pressure prepared samples. Instead, Mott-insulator behavior with anomalous high Pr ordering TN(Pr) = 19 K was observed for PrBa2Cu3O6.95. Comparison with other Pr/Ba intersubstituted Pr1-xBa2-xCu3O7-y cuprates is discussed.

AB - High oxygen pressure annealed PrBa2Cu3O7-y (y∼0) cuprates were prepared in order to study the effect of oxygen stoichiometric parameter y on the unusual Pr/Cu magnetic properties and/or recently reported superconductivity. The oxygen-rich orthorhombic 123-chain phase is highly unstable under high-oxygen pressure synthesis and decomposes completely in 10 bar pressure. For a smaller 2 bar prepared sample a relatively clean phase was preserved with an oxygen parameter y = 0.05, as compared with y = 0.11 from a conventional 1 bar flowing oxygen method. No superconductivity can be detected for all high-oxygen pressure prepared samples. Instead, Mott-insulator behavior with anomalous high Pr ordering TN(Pr) = 19 K was observed for PrBa2Cu3O6.95. Comparison with other Pr/Ba intersubstituted Pr1-xBa2-xCu3O7-y cuprates is discussed.

UR - http://www.scopus.com/inward/record.url?scp=0035356830&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0035356830&partnerID=8YFLogxK

U2 - 10.1063/1.1357859

DO - 10.1063/1.1357859

M3 - Conference article

AN - SCOPUS:0035356830

SN - 0021-8979

VL - 89

SP - 7484

EP - 7486

JO - Journal of Applied Physics

JF - Journal of Applied Physics

IS - 11 II

T2 - 8th Joint Magnetism and Magnetic Materials-Intermag Conference

Y2 - 7 January 2001 through 11 January 2001

ER -

Magnetic properties of high-oxygen pressure prepared PrBa2Cu3O7-y cuprates

摘要

ASJC Scopus subject areas

存取文件

其它文件與鏈接

指紋

引用此

Magnetic properties of high-oxygen pressure prepared PrBa₂Cu₃O_7-y cuprates