Magnetic properties and microscopic structures of ultrathin Co/√3 × √3 - R30°-Ag/Si(111) films

Jyh Shen Tsay, Tsu Yi Fu*, Chih Kuei Kao, Xiao Lan Huang, Jyh Ron Shue, Wei Hsiang Chen, Yeong Der Yao

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

3 引文 斯高帕斯(Scopus)

摘要

Combined scanning tunneling microscopy and surface magneto-optic Kerr effect studies were employed to study the relation between magnetic properties and the microscopic interfacial structures of ultrathin Co/√3 × √3 - R30°-Ag/Si(111) films. On the top of √3 × √3 - R30°-Ag/Si(111), pure Co clusters formed without disrupting the √3 × √3 - R30° structure of the Ag buffer layer. The great strain due to the large mismatch between Co and the substrate influenced the nucleation of Co atoms to form large clusters. No magnetic hysteresis in the polar configuration was observed for films thinner than 10 monolayers. The easy axis of magnetization was in the surface plane. Capping √3 × √3 - R30°-Ag on top of the Si(111) surface before the deposition of the Co overlayers can efficiently reduce the nonferromagnetic Co-Si compound to zero thickness. For Co coverage between 2.9 and 4.2 monolayers, a lower Curie temperature was observed in ultrathin films. Due to the existence of a smooth interface between Co and the √3 × √3 - R30°-Ag buffer, the coercivity for Co/√3 × √3 - R30°-Ag/Si(111) is smaller than that for Co/Si(111).

原文英語
頁(從 - 到)1792-1796
頁數5
期刊Journal of the Korean Physical Society
62
發行號12
DOIs
出版狀態已發佈 - 2013 七月

ASJC Scopus subject areas

  • 物理與天文學 (全部)

指紋

深入研究「Magnetic properties and microscopic structures of ultrathin Co/√3 × √3 - R30°-Ag/Si(111) films」主題。共同形成了獨特的指紋。

引用此