Impedance spectroscopic studies on congruent LiNbO3 single crystal

R. H. Chen, Li Fang Chen, Chih Ta Chia

研究成果: 雜誌貢獻文章

32 引文 斯高帕斯(Scopus)

摘要

Electrical impedance measurements on a congruent LiNbO3 single crystal were performed as a function of both temperature and frequency. The measurements were carried out in the directions along the c-and a-axes of the crystal. The temperature and frequency dependence of various dielectric properties have been studied. The result has revealed two remarkable dynamic relaxations: dielectric dipolar relaxation and ionic conductivity relaxation. The dipolar relaxation peaks were found at frequencies around 4 × 10 6 and 2 × 106Hz for the c-axis and a-axis, respectively, and they were only slightly temperature dependent. The ionic conductivity relaxation was found at the lower-frequency end but it was temperature dependent. The temperature dependence of the dc electrical conductivity follows the Arrhenius law. It corresponds to the long-range ionic motion of Li+ ions which are thermally activated with activation energy of 0.90 and 0.87eV along the c-and a-axis directions, respectively. The dc conductivities measured along the c-and a-axes are very close to each other, and the value increases from 1.7 × 10-6 to 1.9 × 10 -3Ω-1cm-1 as the temperature is raised from 300 to 700 °C. The sample crystal becomes an ionic conductor as the temperature is raised.

原文英語
文章編號086225
期刊Journal of Physics Condensed Matter
19
發行號8
DOIs
出版狀態已發佈 - 2007 二月 28

ASJC Scopus subject areas

  • Materials Science(all)
  • Condensed Matter Physics

指紋 深入研究「Impedance spectroscopic studies on congruent LiNbO<sub>3</sub> single crystal」主題。共同形成了獨特的指紋。

  • 引用此