Hydrothermal synthesis and characterization of two new microporous zinc-substituted gallium phosphates templated by diaminocyclohexane: (H2DACH)2[Zn4Ga2 (HPO4)3(PO4)4] and (H2DACH)[Zn2Ga2 (PO4)4]

C. H. Lin, S. L. Wang*

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

20 引文 斯高帕斯(Scopus)

摘要

Two new zinc-substituted gallophosphates, (H2DACH)2[Zn4Ga2(HPO4) 3(PO4)4] (1) and (H2DACH)[Zn2Ga2(PO4)4] (2), have been synthesized under mild hydrothermal conditions and characterized by single-crystal X-ray diffraction, solid-state NMR spectroscopy, and thermogravimetric analysis. Both structures are built up with MO4 (M = Zn, Ga) and PO4 (or HPO4) tetrahedra. Compound 1 adopts a novel microporous framework which contains the highest transition-metal concentration of any MGaPO. The structure may be viewed as stacking of [Zn2Ga(HPO4)2 (PO4)2]2 layers along a linked by extra HPO4 tetrahedra as pillars to generate intersecting 12-ring channels with dimensions ∼8.1 × 8.1 Å. Compound 2 has a CGS framework topology but a higher divalent-metal content than the isostructural materials of (C7NH14)[MGa3P4O12] (M = Co, Zn). Diprotonated 1,2-diaminocyclohexane (DACH) cations are ordered at the intersections of two interconnected channels in both 1 and 2. They represent the first zinc-substituted gallophosphate templated by dibasic amine and showing distinguishable Zn sites. The solid-state 31P MAS NMR spectrum of 1 showed a resonance for the HPO4/2- group that was shifted downfield by ∼8 ppm relative to the PO4/3- group. On the basis of the results of TG/DT analyses, both frameworks can be thermally stable up to ∼300 °C. Crystal data: 1, monoclinic, C2/c, a = 23.568(1) Å, b = 10.242(1) Å, c = 16.235(1) Å, β = 108.115(1)°, Z = 4; 2, monoclinic, P21/c, a = 14.320(1) Å, b = 16.255(1) Å, c = 8.855(1) Å, β = 90.134(1)°, Z = 4.

原文英語
頁(從 - 到)3617-3623
頁數7
期刊Chemistry of Materials
12
發行號12
DOIs
出版狀態已發佈 - 2000
對外發佈

ASJC Scopus subject areas

  • 化學 (全部)
  • 化學工程 (全部)
  • 材料化學

指紋

深入研究「Hydrothermal synthesis and characterization of two new microporous zinc-substituted gallium phosphates templated by diaminocyclohexane: (H<sub>2</sub>DACH)<sub>2</sub>[Zn<sub>4</sub>Ga<sub>2</sub> (HPO<sub>4</sub>)<sub>3</sub>(PO<sub>4</sub>)<sub>4</sub>] and (H<sub>2</sub>DACH)[Zn<sub>2</sub>Ga<sub>2</sub> (PO<sub>4</sub>)<sub>4</sub>]」主題。共同形成了獨特的指紋。

引用此