Hydrogen-Controlled Spin Reorientation Transition in a Nanometer-Thick FePd Layer on Co/[Pt/Co]4/Pt Multilayers for Applications in Spintronics

Kun Jen Hsueh; Po Chun Chang; Li Jie Liaw; Alltrin Dhanarajagopal; Minn Tsong Lin; Wen Chin Lin

doi:10.1021/acsanm.2c05095

Hydrogen-Controlled Spin Reorientation Transition in a Nanometer-Thick FePd Layer on Co/[Pt/Co]₄/Pt Multilayers for Applications in Spintronics

Kun Jen Hsueh, Po Chun Chang, Li Jie Liaw, Alltrin Dhanarajagopal, Minn Tsong Lin^*, Wen Chin Lin^*

^*此作品的通信作者

物理學系

研究成果: 雜誌貢獻 › 期刊論文 › 同行評審

8 引文斯高帕斯（Scopus）

摘要

In this study, we deposited a hydrogen-sensitive FePd alloy film on Co/[Pt/Co]₄/Pt multilayers with perpendicular magnetic anisotropy (PMA). Through hydrogenation, spin-reorientation transition (SRT) from a perpendicular to an in-plane direction was observed in the 2-nm-thick FePd capped multilayer. Magneto-optic Kerr effect measurements were performed in hydrogen gas at pressures ranging from a vacuum of 5 × 10^-3 mbar to H₂ gas at 200 mbar. Reversible SRT was demonstrated with the cyclic change of H₂ pressure. Furthermore, tuning the strength of the PMA multilayer by adjusting the thickness of the Pt layer changed the SRT-critical thickness of the FePd cap and the hydrogen-induced SRT behavior. These findings will be valuable for application in spintronics through the electronic control of H-migration.

原文	英語
頁（從 - 到）	2784-2790
頁數	7
期刊	ACS Applied Nano Materials
卷	6
發行號	4
DOIs	https://doi.org/10.1021/acsanm.2c05095
出版狀態	已發佈 - 2023 2月 24

ASJC Scopus subject areas

一般材料科學

存取文件

10.1021/acsanm.2c05095

其它文件與鏈接

Link to publication in Scopus

引用此

@article{1d294a15aa444c0eb09bfc021f2ef48e,

title = "Hydrogen-Controlled Spin Reorientation Transition in a Nanometer-Thick FePd Layer on Co/[Pt/Co]4/Pt Multilayers for Applications in Spintronics",

abstract = "In this study, we deposited a hydrogen-sensitive FePd alloy film on Co/[Pt/Co]4/Pt multilayers with perpendicular magnetic anisotropy (PMA). Through hydrogenation, spin-reorientation transition (SRT) from a perpendicular to an in-plane direction was observed in the 2-nm-thick FePd capped multilayer. Magneto-optic Kerr effect measurements were performed in hydrogen gas at pressures ranging from a vacuum of 5 × 10-3 mbar to H2 gas at 200 mbar. Reversible SRT was demonstrated with the cyclic change of H2 pressure. Furthermore, tuning the strength of the PMA multilayer by adjusting the thickness of the Pt layer changed the SRT-critical thickness of the FePd cap and the hydrogen-induced SRT behavior. These findings will be valuable for application in spintronics through the electronic control of H-migration.",

keywords = "hydrogen absorption, magnetic thin film, multilayer, perpendicular magnetic anisotropy, spin reorientation transition",

author = "Hsueh, {Kun Jen} and Chang, {Po Chun} and Liaw, {Li Jie} and Alltrin Dhanarajagopal and Lin, {Minn Tsong} and Lin, {Wen Chin}",

note = "Publisher Copyright: {\textcopyright} 2023 American Chemical Society.",

year = "2023",

month = feb,

day = "24",

doi = "10.1021/acsanm.2c05095",

language = "English",

volume = "6",

pages = "2784--2790",

journal = "ACS Applied Nano Materials",

issn = "2574-0970",

publisher = "American Chemical Society",

number = "4",

}

TY - JOUR

T1 - Hydrogen-Controlled Spin Reorientation Transition in a Nanometer-Thick FePd Layer on Co/[Pt/Co]4/Pt Multilayers for Applications in Spintronics

AU - Hsueh, Kun Jen

AU - Chang, Po Chun

AU - Liaw, Li Jie

AU - Dhanarajagopal, Alltrin

AU - Lin, Minn Tsong

AU - Lin, Wen Chin

PY - 2023/2/24

Y1 - 2023/2/24

N2 - In this study, we deposited a hydrogen-sensitive FePd alloy film on Co/[Pt/Co]4/Pt multilayers with perpendicular magnetic anisotropy (PMA). Through hydrogenation, spin-reorientation transition (SRT) from a perpendicular to an in-plane direction was observed in the 2-nm-thick FePd capped multilayer. Magneto-optic Kerr effect measurements were performed in hydrogen gas at pressures ranging from a vacuum of 5 × 10-3 mbar to H2 gas at 200 mbar. Reversible SRT was demonstrated with the cyclic change of H2 pressure. Furthermore, tuning the strength of the PMA multilayer by adjusting the thickness of the Pt layer changed the SRT-critical thickness of the FePd cap and the hydrogen-induced SRT behavior. These findings will be valuable for application in spintronics through the electronic control of H-migration.

AB - In this study, we deposited a hydrogen-sensitive FePd alloy film on Co/[Pt/Co]4/Pt multilayers with perpendicular magnetic anisotropy (PMA). Through hydrogenation, spin-reorientation transition (SRT) from a perpendicular to an in-plane direction was observed in the 2-nm-thick FePd capped multilayer. Magneto-optic Kerr effect measurements were performed in hydrogen gas at pressures ranging from a vacuum of 5 × 10-3 mbar to H2 gas at 200 mbar. Reversible SRT was demonstrated with the cyclic change of H2 pressure. Furthermore, tuning the strength of the PMA multilayer by adjusting the thickness of the Pt layer changed the SRT-critical thickness of the FePd cap and the hydrogen-induced SRT behavior. These findings will be valuable for application in spintronics through the electronic control of H-migration.

KW - hydrogen absorption

KW - magnetic thin film

KW - multilayer

KW - perpendicular magnetic anisotropy

KW - spin reorientation transition

UR - http://www.scopus.com/inward/record.url?scp=85171731331&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=85171731331&partnerID=8YFLogxK

U2 - 10.1021/acsanm.2c05095

DO - 10.1021/acsanm.2c05095

M3 - Article

AN - SCOPUS:85171731331

SN - 2574-0970

VL - 6

SP - 2784

EP - 2790

JO - ACS Applied Nano Materials

JF - ACS Applied Nano Materials

IS - 4

ER -

Hydrogen-Controlled Spin Reorientation Transition in a Nanometer-Thick FePd Layer on Co/[Pt/Co]4/Pt Multilayers for Applications in Spintronics

摘要

ASJC Scopus subject areas

存取文件

其它文件與鏈接

指紋

引用此

Hydrogen-Controlled Spin Reorientation Transition in a Nanometer-Thick FePd Layer on Co/[Pt/Co]₄/Pt Multilayers for Applications in Spintronics