Hole states of hot-pressed samples of La2-xSrxCuO4-δ X-ray absorption spectroscopy studies

S. B. Lee, C. N. Chang, C. H. Hsieh, C. T. Liu

研究成果: 雜誌貢獻文章

1 引文 斯高帕斯(Scopus)


A series of samples of La2-xSrxCuO4 with x = 0, 0.10, 0.15, 0.20, and 0.30, had been prepared in the ambient pressure (AP). The AP samples were annealed under high pressure (2.0 GPa), with and without adding oxidant, to obtain hot-pressed (HP) samples. The lattice structures of the HP samples were observed to be similar to the AP samples, while Tc was found to decrease but the one with x = 0.30 became superconducting. The O-1s and the Cu-2p3/2 X-ray near-edge-absorption spectra (XNEAS) are measured for all as prepared samples, by using synchrotron radiation. Both spectra indicate that the number of holes is depleted after the hot-press treatment. The depletion of holes is found mainly due to the depletion of oxygen. The correlation of Tc with the number of holes, as derived from the O-1s XNEAS, is found not universal. It can be grouped according to the Sr content, x, a new phenomenon that is not seen before.

頁(從 - 到)46-54
期刊Physica C: Superconductivity and its applications
出版狀態已發佈 - 2001 二月 1

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Condensed Matter Physics
  • Energy Engineering and Power Technology
  • Electrical and Electronic Engineering

指紋 深入研究「Hole states of hot-pressed samples of La<sub>2-x</sub>Sr<sub>x</sub>CuO<sub>4-δ</sub> X-ray absorption spectroscopy studies」主題。共同形成了獨特的指紋。

  • 引用此