High-yield production of graphene flakes using a novel electrochemical/mechanical hybrid exfoliation

Tun Ping Teng, Sheng Chang Chang, Zi Ying Chen, Chun Kai Huang, Shih Feng Tseng, Chii Rong Yang

研究成果: 雜誌貢獻文章

摘要

This research aims to develop a novel hybrid process of an electrochemical intercalation and mechanical exfoliation for fabricating graphene flakes. Using a rotational tool as electrode, the graphite powders were electrochemically intercalated using ions in electrolyte, and then the expanded graphite powders were mechanically exfoliated for few-layer graphene flakes. To obtain the high-quality graphene flakes, the graphite powders were intercalated in the mixed electrolyte of myristyl alcohol surfactant added in H2SO4 solution at the speed of the rotational tool of 2000 rpm and the applied voltage of ± 4 V for 1 h, and then the expanded graphite powders were mechanically exfoliated at the speed of the rotational tool of 10000 rpm for 1 h. The average thickness and lateral size of the graphene flakes was 1.42 nm and 0.5 μm measured by an atomic force microscope, respectively. The maximum C/O and I2D/IG ratios of graphene flakes were 22.29 and 1.22 analyzed by an X-ray photoelectron spectroscope and a Raman spectrometer, respectively. Besides, the production yield of the exfoliated few-layer graphene flakes was evaluated that could achieve to 20%, which was approximately 2 times more than the pure electrochemical or pure mechanical exfoliation methods.

原文英語
頁(從 - 到)2751-2760
頁數10
期刊International Journal of Advanced Manufacturing Technology
104
發行號5-8
DOIs
出版狀態已發佈 - 2019 十月 1

ASJC Scopus subject areas

  • Control and Systems Engineering
  • Software
  • Mechanical Engineering
  • Computer Science Applications
  • Industrial and Manufacturing Engineering

指紋 深入研究「High-yield production of graphene flakes using a novel electrochemical/mechanical hybrid exfoliation」主題。共同形成了獨特的指紋。

  • 引用此