High-performance poly(2,3-diphenyl-1,4-phenylene vinylene)-based polymer light-emitting diodes by blade coating method

Yung Ming Liao, Hung Min Shih, Kuang Hui Hsu, Chain Shu Hsu, Yu Chiang Chao, Sheng Chia Lin, Chun Yao Chen, Hsin Fei Meng

    研究成果: 雜誌貢獻期刊論文同行評審

    14 引文 斯高帕斯(Scopus)

    摘要

    A new series of super high brightness and luminance efficient poly(2,3-diphenyl-1,4-phenylene vinylene) (DP-PPV)-based electroluminescent (EL) polymers containing methoxy or long branched alkoxy chains were synthesized via Gilch polymerization. The branched alkoxy groups were introduced to enhance solubility for blade and spin-coating processes. Monomers of DMeO-PPV and m-Ph-PPV were used to increase steric hindrance and prevent close packing of the main chain. By controlling the feeding ratio of different monomers during polymerization, DP-PPV derivatives with high molecular weight were obtained. All synthesized polymers possess high glass transition temperatures and thermal stabilities. The maximum photoluminescent emissions of the thin films are located between 544 and 547 nm. Cyclic voltammetry analysis reveals that the band gaps of these light-emitting materials are in the range of 2.75-2.84 eV. Blade coating was used to fabricate multilayer polymer light-emitting diodes. A multilayer electroluminescent device with the configuration of ITO/PEDOT:PSS/TFB/P1/TPBi/LiF/Al exhibited a very high luminescence efficiency (10.96 cd A-1). The maximum brightness of the multilayer EL device ITO/PEDOT:PSS/TFB/P3/CsF/Al reached up to 78,050 cd m-2 with a low turn-on voltage (4.0 V). For further investigation, polymer P3 was blended with DPPFBNA to achieve white light-emitting device; the multilayer devices generated a maximum brightness of 1085 cd m-2 and a luminance efficiency of 0.75 cd A-1, with CIE coordinates (0.28, 0.33) at 11 V.

    原文英語
    頁(從 - 到)3717-3724
    頁數8
    期刊Polymer
    52
    發行號17
    DOIs
    出版狀態已發佈 - 2011 八月 3

    ASJC Scopus subject areas

    • Organic Chemistry
    • Polymers and Plastics
    • Materials Chemistry

    指紋 深入研究「High-performance poly(2,3-diphenyl-1,4-phenylene vinylene)-based polymer light-emitting diodes by blade coating method」主題。共同形成了獨特的指紋。

    引用此