Growth, thermal stability and magnetism of Ni ultrathin films on O-3 × 3/W(1 1 1) surface

Cheng Jui Tsai, Kun Jen Hsueh, N. Plusnin, Chien Cheng Kuo, Wen Chin Lin

研究成果: 雜誌貢獻文章同行評審

4 引文 斯高帕斯(Scopus)

摘要

In this study, a well ordered O-3 × 3 superstructure was prepared on a W(1 1 1) surface for the investigation of the growth, thermal stability and magnetism of Ni ultrathin films on it. During the deposition and thermal annealing, Auger signal of oxygen was nearly invariant, indicating that the oxygen played a role of surfactant in this system. Due to the large lattice mismatch between the Ni films and W(1 1 1) substrate (3.95%), Ni underwent an island-growth, which was considerably affected by the growth temperature. After annealing at 500-800 K, the Auger signal ratio of Ni/W significantly decreased to approximately 1, indicating the formation of 3-dimensional islands with a wetting thickness of one pseudomorphic layer. Subsequent annealing to 800-1200 K annealing led to the more serious aggregation, i.e. de-wetting of Ni layer. The 3 and 11.5 PML Ni films revealed a stable canted magnetization, which was possibly attributed to the magneto-elastic anisotropy in the Ni films.

原文英語
頁(從 - 到)166-171
頁數6
期刊Applied Surface Science
313
DOIs
出版狀態已發佈 - 2014 九月 15

ASJC Scopus subject areas

  • Chemistry(all)
  • Condensed Matter Physics
  • Physics and Astronomy(all)
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

指紋 深入研究「Growth, thermal stability and magnetism of Ni ultrathin films on O-3 × 3/W(1 1 1) surface」主題。共同形成了獨特的指紋。

引用此