Growth of epitaxial needlelike ZnO nanowires on GaN films

Yung Kuan Tseng, Chih Ta Chia, Chien Yih Tsay, Li Jiaun Lin, Hsin Min Cheng, Chung Yi Kwo, I. Cherng Chen

研究成果: 雜誌貢獻期刊論文同行評審

27 引文 斯高帕斯(Scopus)

摘要

Epitaxial needlelike ZnO nanowires were grown vertically over an entire epi-GaN/sapphire substrate at 550°C by low-pressure vapor phase deposition without employing any metal catalysts. A two-step oxygen injection process is the key of successful synthesis. The length of ZnO wires was up to 3.0 μm. The diameters of the roots and tips of the ZnO nanowires were around 80-100 and 15-30 nm, respectively. X-ray diffraction showed the epitaxial orientation relationship between ZnO and GaN as [001]Zno//[001]GiN along the normal to the plane, and [100]Zno//[100]GaN along the in-plane direction, consistent with the selective area electron diffraction pattern taken at the ZnO/GaN heterointerface. High-resolution transmission electron microscopy confirmed that nanowire was a single crystal. A room-temperature photoluminescence spectrum of the wires revealed a low concentration of oxygen vacancy in the ZnO nanowires and showed high optical quality.

原文英語
頁(從 - 到)G95-G98
期刊Journal of the Electrochemical Society
152
發行號1
DOIs
出版狀態已發佈 - 2005 二月 7

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Renewable Energy, Sustainability and the Environment
  • Surfaces, Coatings and Films
  • Electrochemistry
  • Materials Chemistry

指紋 深入研究「Growth of epitaxial needlelike ZnO nanowires on GaN films」主題。共同形成了獨特的指紋。

引用此