Growth mechanism of Ni on Pt(110) at low temperature

Ching-Song Shern*, J. S. Tsay, Tsu Yi Fu

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

7 引文 斯高帕斯(Scopus)

摘要

Ni atoms deposited on Pt(110)-(1 × 1) and (1 × 2) surfaces are studied and compared at 130 K. The Auger uptake curve of Ni on the Pt(110)-(1 × 1) surface shows an exponential-type growth. The intensities of all (1 × 1) LEED spots decrease gradually and exhibit no oscillation during the deposition. These results demonstrate that this growth follows the Volmer-Weber mode. On the other hand, the Auger uptake curve of Ni on the Pt(110)-(1 × 2) surface shows a premonolayer break with an initial linear growth. The LEED pattern changes from (1 × 2) to a pseudo-(1 × 1) after Ni atoms fill the sites of the missing rows. After that, the Auger uptake curve turns to an exponential-type and the LEED spot patterns all diminish gradually when more Ni atoms are deposited on the Pt(110)-(1 × 2) surface. These results demonstrate that the growth of Ni on the Pt(110)-(1 × 2) surface follows the Stranski-Krastanov (SK) mode. The growth mechanism is discussed by considering the lattice mismatch, diffusion, and the surface free energies of the adsorbate and the substrate.

原文英語
頁(從 - 到)74-78
頁數5
期刊Applied Surface Science
92
DOIs
出版狀態已發佈 - 1996 二月

ASJC Scopus subject areas

  • 化學 (全部)
  • 凝聚態物理學
  • 物理與天文學 (全部)
  • 表面和介面
  • 表面、塗料和薄膜

指紋

深入研究「Growth mechanism of Ni on Pt(110) at low temperature」主題。共同形成了獨特的指紋。

引用此