Growth and magnetism of low-temperature deposited Fe/Si(111) films as an intermediate layer for suppression of silicide formation

Wen Ting Tu, Chih Hsiung Wang, Ya Yun Huang, Wen-Chin Lin

研究成果: 雜誌貢獻文章

14 引文 斯高帕斯(Scopus)

摘要

Low temperature (LT: 100 K) deposition of Fe on Si (111) 7×7 surface effectively reduces Fe-silicide formation at the Fe/Si interface, as compared with conventional room temperature (RT) growth. The interface condition of 5-15 monolayers (ML) LT-Fe/Si(111) remains stable at least up to 350 K. Si segregation was observed after annealing at 400 K. LT-grown Fe films also reveal a relatively flat surface morphology with a roughness of 0.4-0.6 nm. Thus, LT-Fe films were suggested as an intermediate layer for the subsequent RT-growth of Fe. We use a single domain model of magnetic anisotropy to fit the magnetic coercivity evolution of n ML RT-Fe on 5 ML LT-Fe/Si(111). Accordingly, we deduce the surface and volume-contributed magnetic anisotropy for discussion.

原文英語
文章編號023908
期刊Journal of Applied Physics
109
發行號2
DOIs
出版狀態已發佈 - 2011 一月 15

ASJC Scopus subject areas

  • Physics and Astronomy(all)

指紋 深入研究「Growth and magnetism of low-temperature deposited Fe/Si(111) films as an intermediate layer for suppression of silicide formation」主題。共同形成了獨特的指紋。

引用此