Growth and alloy formation of ultrathin Ni films on Co/Pt(1 1 1)

H. Y. Ho, Y. J. Chen, C. S. Shern

研究成果: 雜誌貢獻文章同行評審

4 引文 斯高帕斯(Scopus)

摘要

Low-energy electron diffraction (LEED) and Auger electron spectroscopy (AES) were used to study the growth and the structural evolution of Ni/Co/Pt(1 1 1) following high-temperature annealing. From the oscillation of the specular beam of the LEED and Auger uptake curve, we concluded that the growth mode of thin Ni films on 1 ML Co/Pt(1 1 1) is at least 2 ML layer-by-layer growth before three-dimensional island growth begins. The alloy formation of Ni/1 ML Co/Pt(1 1 1) was analyzed by AES. The temperature for the intermixing of Ni and Co layers in the upper interface without diffusing into the bulk of Pt is independent of the thickness of Ni when a Co buffer is one atomic monolayer. After the temperature was increased, formations of Ni-Co-Pt alloy, Ni-Pt alloy and Co-Pt alloy were observed. The temperature required for the Ni-Co intermixing layer to diffuse into Pt bulk increases with the thickness of Ni. The interlayer distance as a function of annealing temperature for 1 ML Ni/1 ML Co/Pt(1 1 1) was calculated from the I-V LEED. The evolution of LEED patterns was also observed at different annealing temperatures.

原文英語
頁(從 - 到)1093-1098
頁數6
期刊Surface Science
600
發行號5
DOIs
出版狀態已發佈 - 2006 三月 1

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Materials Chemistry

指紋 深入研究「Growth and alloy formation of ultrathin Ni films on Co/Pt(1 1 1)」主題。共同形成了獨特的指紋。

引用此