摘要
All-solid-state Li-ion batteries (ASSLIBs), also known as next-generation batteries, have attracted much attention due to their high energy density and safety. The best advantage of ASSLIBs is the Li-metal anodes that could be used without safety issues. In this study, a highly conductive garnet solid electrolyte (Li6.75La3Zr1.75Ta0.25O12, LLZTO) was used in the ASSLIB, and a Pt film was used to modify the surface of LLZTO to prove the solution of the Li-metal anode for LLZTO. Li-Pt alloy was synthesized to improve the wettability and contact of the interface. The interfacial resistance was reduced by 21 times, at only 9 ω cm2. The symmetric cell could stably cycle over 3500 h at a current density of 0.1 mA cm-2. The full cell of Li|Li-Pt|LLZTO|LiFePO4 and Li|Li-Pt|LLZTO|LiMn0.8Fe0.2PO4 achieved high stability in terms of battery performance. Point-to-point contact transformed into homogeneous surface contact made the Li-ion flux faster and more stable. This surface modification method could provide researchers with a new choice for fixing interface issues and promoting the application of high-performance ASSLIBs in the future.
原文 | 英語 |
---|---|
頁(從 - 到) | 56181-56190 |
頁數 | 10 |
期刊 | ACS Applied Materials and Interfaces |
卷 | 13 |
發行號 | 47 |
DOIs | |
出版狀態 | 已發佈 - 2021 12月 1 |
ASJC Scopus subject areas
- 材料科學(全部)