Experimental study on thermal conductivity of lubricant containing nanoparticles

Ching Song Jwo, Lung Yue Jeng*, Ho Chang, Tun-Ping Teng


研究成果: 雜誌貢獻期刊論文同行評審

21 引文 斯高帕斯(Scopus)


In this study, the Al2O3 nanofluids produced from the direct synthesis method were used as the experimental samples, and ultrasonic vibration was used for dispersing the nanoparticles into three types of different weight fractions (1.0, 1.5, 2.0 wt.%). The base solvent was the lubricant of R-134a refrigeration system. The objectives of this study were to discuss the dependence of thermal conductivity of Al2O3 nanofluids on the temperature (20-40 °C) under different weight fractions. This experiment used the thermostatic bath to stabilize the temperature of sample, and the transient hot-wire method to measure the thermal conductivity in the nanofluids of different weight fractions and sample temperature. The results showed that the thermal conductivities were enhanced by 2.0%, 4.6%, and 2.5% when the nanoparticles of Al2O3 of 1.0, 1.5, and 2.0 wt.% were added at 40 °C. Among them, the optimal enhancement of the thermal conductivity was at 1.5 wt.%. The enhancement of thermal conductivity did not grow with the increase of weight ratios, and it was obviously different from the general nanofluids with lubricant as the basic solvent. Besides, thermal conductivities increased from 1.5 to 4.6% when the sample temperatures were from 20 °C to 40 °C at 1.5 wt.%, and the trend of growth rates of the thermal conductivity was proportional to temperature. From the results, it can be realized that temperature has greater effects than weight fraction on the increase of thermal conductivities. Thus, it is better for nanpfluids of Al2O3 to be applied in the high temperature field than in the low temperature field.

頁(從 - 到)662-668
期刊Reviews on Advanced Materials Science
出版狀態已發佈 - 2008 十二月 1

ASJC Scopus subject areas

  • 材料科學(全部)
  • 凝聚態物理學


深入研究「Experimental study on thermal conductivity of lubricant containing nanoparticles」主題。共同形成了獨特的指紋。