Evidences of defect contribution in magnetically ordered Sm-implanted GaN

Fang Yuh Lo, Jhong Yu Guo, Cheng De Huang, Kai Chieh Chou, Hsiang Lin Liu, Verena Ney, Andreas Ney, Ming Yau Chern, Stepan Shvarkov, Dirk Reuter, Andreas D. Wieck, Sébastien Pezzagna, Jean Massies

研究成果: 雜誌貢獻期刊論文同行評審

3 引文 斯高帕斯(Scopus)

摘要

Samarium (Sm) ions of 200 keV in energy were implanted into highly-resistive molecular-beam-epitaxy grown GaN thin films with a focused-ion-beam implanter at room temperature. The implantation doses range between 1014 and 1016 cm-2. X-ray diffraction revealed Sm incorporation into GaN matrix without secondary phase. Raman-scattering spectroscopy identified impurity-independent defect-related oscillation modes. Slight decrease in band gap and significant reduction in transmittance were observed by optical transmission spectroscopy. Photoluminescence spectra showed emission peaks related to background p-type impurity. Ferromagnetic hysteresis loops were recorded from GaN implanted with highest Sm dose, and magnetic ordering was observed from Sm-implanted GaN with dose of and above 1015 cm-2. The long-range magnetic ordering can be attributed to interaction of Sm ions through the implantation-induced Ga vacancy.

原文英語
頁(從 - 到)S7-S11
期刊Current Applied Physics
14
發行號SUPPL. 1
DOIs
出版狀態已發佈 - 2014 三月 14

ASJC Scopus subject areas

  • Materials Science(all)
  • Physics and Astronomy(all)

指紋 深入研究「Evidences of defect contribution in magnetically ordered Sm-implanted GaN」主題。共同形成了獨特的指紋。

引用此