Electroluminescence from a conjugated polymer grafted with CdSe/ZnS: High brightness and improved efficiency

Kuei Bai Chen, Ming Hwey Chen, Sheng Hsiung Yang, Chao Hsiang Hsieh, Chain Shu Hsu*, Chia Chun Chen, Hsiao Ju Chien

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

19 引文 斯高帕斯(Scopus)

摘要

A new series of sulfide-substituted poly(1,4-phenylene vinylene) derivatives (S1PPV-S3PPV) with different composition ratios were successfully synthesized via the Gilch route. The CdSe/ZnS were grafted to the sulfur atoms by ligand exchange reaction. The grafted CdSe/ZnS contents were determined from TGA analysis to be from 4.6 to 37.8%. A new peak at 1151 cm-1 formed in FT-IR after ligand exchange, which is attributed to the force formation between sulfur and CdSe. The GPC results show that the molecular weights of final polymers became higher after ligand exchange. Thin films of obtained polymers emitted bright green and yellow light with the max emission peak located from 546 to 556 nm. Double-layer LEDs with an ITO/PEDOT/polymer/Ca/Al configuration were fabricated to evaluate the potential use of these polymers. The turn-on voltages of the devices were about 4-5 V. As the CdSe/ZnS content increased in grafted polymers, the device performance was significantly enhanced as compared to pristine polymers. In the case of S3PPV, the double-layer device showed a maximum luminance of 6073 cd/m2 with a current yield of 0.82 cd/A. The maximum luminance and current yield was enhanced to 13,390 cd/m2 and 2.25 cd/A by grafting CdSe/ZnS onto polymers.

原文英語
頁(從 - 到)5378-5390
頁數13
期刊Journal of Polymer Science, Part A: Polymer Chemistry
44
發行號18
DOIs
出版狀態已發佈 - 2006 九月 15

ASJC Scopus subject areas

  • 聚合物和塑料
  • 有機化學
  • 材料化學

指紋

深入研究「Electroluminescence from a conjugated polymer grafted with CdSe/ZnS: High brightness and improved efficiency」主題。共同形成了獨特的指紋。

引用此