Electrochemically fabricated gold dendrites with underpotential deposited silver monolayers for a bimetallic SERS-active substrate

Ying Huang Lai*, Shan Chi Kuo, Yun Ching Hsieh, Yu Chun Tai, Wei Hsiu Hung, U. Ser Jeng

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

11 引文 斯高帕斯(Scopus)

摘要

With electrochemical deposition, cysteine-directed crystalline gold dendrites (Au-Ds) on glassy carbon electrodes were fabricated. The Au-Ds surfaces were further modified with Ag adatoms by underpotential deposition (UPD) for Ag-covered Au-Ds (Ag-Au-Ds). The Ag-Au-Ds possessed a hierarchical architecture comprising trunks, branches, and nanoleaves for a threefold-symmetry, resulting in a high density of sharp tips and edges for hot spots of surface-enhanced Raman scattering (SERS). Prominent SERS was observed with p-nitrothiophenol (p-NTP) adsorption onto either Au-Ds or Ag-Au-Ds, for a best p-NTP detection limit down to 5-10 nM at 785 nm laser excitation. However, at specific 633 nm laser excitation, SERS with p-NTP adsorption on Ag-Au-Ds exhibited a three-fold higher enhancement over that measured for p-NTP adsorbed on unmodified Au-Ds, suggesting an increased chemical SERS enhancement with the Ag-p-NTP bonding. Furthermore, adsorption isotherms of p-NTP with Au-Ds and Ag-Au-Ds adsorption in solution are established from solution p-NTP-concentration dependent SERS; from which, comparable binding constants of p-NTP to Au-Ds and Ag-Au-Ds are extracted.

原文英語
頁(從 - 到)13185-13192
頁數8
期刊RSC Advances
6
發行號16
DOIs
出版狀態已發佈 - 2016

ASJC Scopus subject areas

  • 化學 (全部)
  • 化學工程 (全部)

指紋

深入研究「Electrochemically fabricated gold dendrites with underpotential deposited silver monolayers for a bimetallic SERS-active substrate」主題。共同形成了獨特的指紋。

引用此