Effects of Si capping layers on the properties of ultrathin Co/Ir(111) films

J. S. Tsay, Y. C. Liou, C. M. Chen, W. Y. Chan

研究成果: 雜誌貢獻文章

1 引文 斯高帕斯(Scopus)

摘要

Surface compositions and annealing effects for ultrathin Co/Ir(111) films influenced by Si capping layers have been investigated. On the surface of Co/Ir(111) films, Si adatoms are chemically active in the formation of Co-Si interfaces. Low-energy electron diffraction observations reveal that Si-Co interfaces is disordered in the long range. From sputtering profiling measurements, alloy formations occur at the interfacial layers, while pure cobalt remains on the Ir(111). After depositing submonolayer silicon on Co/Ir(111), the relative easy axis of magnetization in the polar geometry is mainly attributed to the positive interface anisotropy of the Co/Ir interface. The formation of nonmagnetic Co-Si compounds plays a dominant role in reducing the effectiveness of magnetic layers. Below 500 K, the interdiffusion of Si into the underlying Co layer occurs. Further interaction of Si atoms with Co layers and interdiffusion at the Co-Ir interface are observed at higher temperatures. This causes no detectable magnetic hysteresis after annealing up to 800 K.

原文英語
頁(從 - 到)1266-1270
頁數5
期刊Journal of Vacuum Science and Technology A: Vacuum, Surfaces and Films
27
發行號6
DOIs
出版狀態已發佈 - 2009 十一月 16

ASJC Scopus subject areas

  • Condensed Matter Physics
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films

指紋 深入研究「Effects of Si capping layers on the properties of ultrathin Co/Ir(111) films」主題。共同形成了獨特的指紋。

  • 引用此