Effects of Ag contents and deposition temperatures on the electrical and optical behaviors of Ag-doped Cu2O thin films

C. C. Tseng, J. H. Hsieh, S. J. Liu, W. Wu

研究成果: 雜誌貢獻文章

17 引文 斯高帕斯(Scopus)

摘要

Cu2O-Ag thin films were co-deposited by reactive sputtering on glass substrates. During deposition, Ag contents and deposited temperatures were varied. After deposition, a UV-VIS-NIR photometer and a Hall measurement system were used to characterize the optical and electrical properties of these films. The results showed that the Cu2O-Ag thin films had a decreased optical transmittance with the increase of Ag contents. The resistivity was also decreased, which is most likely due to the formation of Ag phase. Through the measurement of photo-induced conductivity, it was found that, when Ag concentration was at 4 at.%, the film had the highest increase in conductivity under light irradiation. This is due to the co-existence of Ag2O and Cu2O. However, when deposited at a temperature higher than room temperature, the photo-induced conductivity of this film became less obvious, apparently due to the dissociation of Ag2O. The results of Photoluminescence (PL) measurement confirmed that the Cu2O-Ag(4 at.%) sample might produce more electron-hole pairs than other samples, which caused the increase of conductivity.

原文英語
頁(從 - 到)1407-1410
頁數4
期刊Thin Solid Films
518
發行號5
DOIs
出版狀態已發佈 - 2009 十二月 31

ASJC Scopus subject areas

  • Electronic, Optical and Magnetic Materials
  • Surfaces and Interfaces
  • Surfaces, Coatings and Films
  • Metals and Alloys
  • Materials Chemistry

指紋 深入研究「Effects of Ag contents and deposition temperatures on the electrical and optical behaviors of Ag-doped Cu<sub>2</sub>O thin films」主題。共同形成了獨特的指紋。

  • 引用此