Effect of wax composition on the injection molding of carbonyliron powder with LDPE

K. C. Hsu*, C. C. Lin, G. M. Lo


研究成果: 雜誌貢獻期刊論文同行評審

10 引文 斯高帕斯(Scopus)


The effect of waxes on the injection molding of carbonyl iron powder with low-density polyethylene (LDPE) have been examined. Four waxes, paraffin wax (PW), polyethylene wax (PEW), carnauba wax (CW) and acrawax (AW) were selected and compared. Experimental results indicated that the LDPE-rich phase was found to be separated from the wax-rich phase in the binder mixture containing AW, CW of PW, Polar AW or CW showed stronger interactions or adsorptions with iron powder than other nonpolar waxes. AW/LDPE and CW/LDPE mixtures appeared to exhibit higher viscosity, greater pseudoplasticity and lower flow activation energy than PW/LDPE and PEW/LDPE mixtures. Tensile bar specimens of all binder mixtures could be injection molded at an injection temperature of around 170-190°C, and a pressure of around 5-6 MPa. Except for the PEW/LDPE mixture the parts derived from the other three binder mixtures showed good surface appearance following debinding and sintering. Specimens based on the PW/LDPE mixture exhibited the highest tensile strength in the resulting sintered parts, followed those based on CW/LDPE, AW/LDPE, and PEW/LDPE mixtures. The difference in tensile strength of each part results from different flow properties of each wax/LDPE mixture.

頁(從 - 到)181-187
期刊Canadian Metallurgical Quarterly
出版狀態已發佈 - 1996

ASJC Scopus subject areas

  • 金屬和合金
  • 工業與製造工程


深入研究「Effect of wax composition on the injection molding of carbonyliron powder with LDPE」主題。共同形成了獨特的指紋。