Effect of sintering temperature on the photoluminescence characteristics of the Nd2O3-doped SnSiO4 phosphor

Chien Chen Diao, Jing Liu, Cheng Fu Yang, Chin Guo Kuo, Cheng Yi Chen, Yun I. Ho

研究成果: 書貢獻/報告類型會議論文篇章

1 引文 斯高帕斯(Scopus)

摘要

In this study, Nd2O3 was used as the dopant and the commercial Sr2SiO4:Nd phosphors was produced by using solid-state reaction method. The Sr2SiO4:Nd phosphors was sintered at the temperature range of 1000°C∼1300°C for 2 h. From the results of X-ray diffraction patterns, even sintered at 1000°C only Sr2SiO4 phase was observed, no secondary and unknown phases were residual in the calcined Sr2SiO4:Nd powders. We had found that the sintering temperature had large effect on the luminescence characteristics of the Nd2O3-doped Sr2SiO4 phosphors. The CIE colorimetric data of Sr2SiO4:Nd phosphors as a function of sintering temperature was also investigated in this study. We found that the Sr2SiO4:Nd phosphors revealed a dark blue or a ultraviolet light.

原文英語
主出版物標題Proceedings of the IEEE International Conference on Advanced Materials for Science and Engineering
主出版物子標題Innovation, Science and Engineering, IEEE-ICAMSE 2016
編輯Teen-Hang Meen, Stephen D. Prior, Artde Donald Kin-Tak Lam
發行者Institute of Electrical and Electronics Engineers Inc.
頁面263-266
頁數4
ISBN(電子)9781509038695
DOIs
出版狀態已發佈 - 2017 二月 2
事件2016 IEEE International Conference on Advanced Materials for Science and Engineering, IEEE-ICAMSE 2016 - Tainan, 臺灣
持續時間: 2016 十一月 122016 十一月 13

出版系列

名字Proceedings of the IEEE International Conference on Advanced Materials for Science and Engineering: Innovation, Science and Engineering, IEEE-ICAMSE 2016

其他

其他2016 IEEE International Conference on Advanced Materials for Science and Engineering, IEEE-ICAMSE 2016
國家臺灣
城市Tainan
期間2016/11/122016/11/13

ASJC Scopus subject areas

  • Hardware and Architecture
  • Civil and Structural Engineering
  • Mechanics of Materials
  • Media Technology
  • Materials Science (miscellaneous)
  • Electronic, Optical and Magnetic Materials

指紋 深入研究「Effect of sintering temperature on the photoluminescence characteristics of the Nd<sub>2</sub>O<sub>3</sub>-doped SnSiO<sub>4</sub> phosphor」主題。共同形成了獨特的指紋。

引用此