Dramatic depression of Curie temperature for magnetic Co/Cu(1 0 0) ultrathin films upon deposition at elevated temperature

C. C. Kuo, C. L. Chiu, Wen-Chin Lin, Minn Tsong Lin

研究成果: 雜誌貢獻文章

12 引文 (Scopus)

摘要

The correlation between the crystalline structures and magnetic properties, such as magnetization and Curie temperature (TC) were investigated systematically by varying the deposition temperature of 2 ML fcc cobalt films on Cu(100) substrate. At variation of the deposition temperature a dramatic change in Curie temperature and coercivity of the films was observed. The drastic raising of Curie temperature were found for the films with the deposition temperatures from 340 K (TC=170 K) down to 275 K (TC=325 K). A simple theoretical estimation was proposed to evaluate the Curie temperature of the films in terms of magnetic moment as well as anisotropy with quantitative success. The enhanced Curie temperature can be attributed to the increase of the magnetic moments due to the alteration of film morphology with various deposition temperatures.

原文英語
頁(從 - 到)121-127
頁數7
期刊Surface Science
520
發行號3
DOIs
出版狀態已發佈 - 2002 十二月 21

指紋

Ultrathin films
Curie temperature
Magnetic moments
Temperature
magnetic moments
temperature
Cobalt
Coercive force
coercivity
Magnetization
Magnetic properties
Anisotropy
cobalt
magnetic properties
Crystalline materials
magnetization
anisotropy
Substrates

ASJC Scopus subject areas

  • Physical and Theoretical Chemistry
  • Condensed Matter Physics
  • Surfaces and Interfaces

引用此文

Dramatic depression of Curie temperature for magnetic Co/Cu(1 0 0) ultrathin films upon deposition at elevated temperature. / Kuo, C. C.; Chiu, C. L.; Lin, Wen-Chin; Lin, Minn Tsong.

於: Surface Science, 卷 520, 編號 3, 21.12.2002, p. 121-127.

研究成果: 雜誌貢獻文章

@article{723ea630654d43bea0bad0ab916f148f,
title = "Dramatic depression of Curie temperature for magnetic Co/Cu(1 0 0) ultrathin films upon deposition at elevated temperature",
abstract = "The correlation between the crystalline structures and magnetic properties, such as magnetization and Curie temperature (TC) were investigated systematically by varying the deposition temperature of 2 ML fcc cobalt films on Cu(100) substrate. At variation of the deposition temperature a dramatic change in Curie temperature and coercivity of the films was observed. The drastic raising of Curie temperature were found for the films with the deposition temperatures from 340 K (TC=170 K) down to 275 K (TC=325 K). A simple theoretical estimation was proposed to evaluate the Curie temperature of the films in terms of magnetic moment as well as anisotropy with quantitative success. The enhanced Curie temperature can be attributed to the increase of the magnetic moments due to the alteration of film morphology with various deposition temperatures.",
keywords = "Cobalt, Copper, Growth, Magnetic films, Surface structure, morphology, roughness, and topography",
author = "Kuo, {C. C.} and Chiu, {C. L.} and Wen-Chin Lin and Lin, {Minn Tsong}",
year = "2002",
month = "12",
day = "21",
doi = "10.1016/S0039-6028(02)02304-X",
language = "English",
volume = "520",
pages = "121--127",
journal = "Surface Science",
issn = "0039-6028",
publisher = "Elsevier",
number = "3",

}

TY - JOUR

T1 - Dramatic depression of Curie temperature for magnetic Co/Cu(1 0 0) ultrathin films upon deposition at elevated temperature

AU - Kuo, C. C.

AU - Chiu, C. L.

AU - Lin, Wen-Chin

AU - Lin, Minn Tsong

PY - 2002/12/21

Y1 - 2002/12/21

N2 - The correlation between the crystalline structures and magnetic properties, such as magnetization and Curie temperature (TC) were investigated systematically by varying the deposition temperature of 2 ML fcc cobalt films on Cu(100) substrate. At variation of the deposition temperature a dramatic change in Curie temperature and coercivity of the films was observed. The drastic raising of Curie temperature were found for the films with the deposition temperatures from 340 K (TC=170 K) down to 275 K (TC=325 K). A simple theoretical estimation was proposed to evaluate the Curie temperature of the films in terms of magnetic moment as well as anisotropy with quantitative success. The enhanced Curie temperature can be attributed to the increase of the magnetic moments due to the alteration of film morphology with various deposition temperatures.

AB - The correlation between the crystalline structures and magnetic properties, such as magnetization and Curie temperature (TC) were investigated systematically by varying the deposition temperature of 2 ML fcc cobalt films on Cu(100) substrate. At variation of the deposition temperature a dramatic change in Curie temperature and coercivity of the films was observed. The drastic raising of Curie temperature were found for the films with the deposition temperatures from 340 K (TC=170 K) down to 275 K (TC=325 K). A simple theoretical estimation was proposed to evaluate the Curie temperature of the films in terms of magnetic moment as well as anisotropy with quantitative success. The enhanced Curie temperature can be attributed to the increase of the magnetic moments due to the alteration of film morphology with various deposition temperatures.

KW - Cobalt

KW - Copper

KW - Growth

KW - Magnetic films

KW - Surface structure, morphology, roughness, and topography

UR - http://www.scopus.com/inward/record.url?scp=0037153657&partnerID=8YFLogxK

UR - http://www.scopus.com/inward/citedby.url?scp=0037153657&partnerID=8YFLogxK

U2 - 10.1016/S0039-6028(02)02304-X

DO - 10.1016/S0039-6028(02)02304-X

M3 - Article

AN - SCOPUS:0037153657

VL - 520

SP - 121

EP - 127

JO - Surface Science

JF - Surface Science

SN - 0039-6028

IS - 3

ER -