Direct Fabrication of Inkjet-Printed Dielectric Film for Metal–Insulator–Metal Capacitors

In this study, an inkjet-printed dielectric film that used a polymer-based SU-8 ink was fabricated for use in a metal–insulator–metal (MIM) capacitor. Thermal treatment of the inkjet-printed SU-8 polymer film affected its surface morphology, chemical structure, and surface wettability. A 20-min soft-bake at 60°C was applied to eliminate inkjet-printed bubbles and ripples. The ultraviolet-exposed SU-8 polymer film was crosslinked at temperatures between 120°C and 220°C and became disordered at 270°C, demonstrated using Fourier-transform infrared spectroscopy. A maximum SU-8 polymer film hard-bake temperature of 120°C was identified, and a printing process was subsequently employed because the appropriate water contact angle of the printed film was 79°. Under the appropriate inkjet printing conditions, the two-transmission-line method was used to extract the dielectric and electrical properties of the SU-8 polymer film, and the electrical behavior of the fabricated MIM capacitor was also characterized.