Dielectric properties of ultra-low sintering temperature Al2O3-BBSZ glass composite

Mei Yu Chen*, Jari Juuti, Chi Shiung Hsi, Chih Ta Chia, Heli Jantunen

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

41 引文 斯高帕斯(Scopus)

摘要

Ceramic composites of B2O3-Bi2O3-SiO2-ZnO (BBSZ) glass mixed with Al2O3 (10-50 vol%) were sintered at 450°C, and their microstructural and dielectric properties investigated. Dense structures were obtained when the Al2O3 content was lower than 30 vol%. Raman, XRD, and FESEM showed the existence of a secondary phase, Bi24Si2O40, in all samples. The dielectric properties of the composite with 30 vol% addition of Al2O3 showed good dielectric properties with εr of 14.8 and 20.8 and 32.5 at 100 kHz and 100 MHz and 1 GHz, respectively. The tanδ values at the same frequencies were 0.004 and 0.006 and 0.016. The results show that BBSZ glass with different amounts of Al2O3 exhibit widely applicable relative permittivity values and affordable loss and are thus promising candidates for ultra-low sintering temperature applications.

原文英語
頁(從 - 到)1133-1136
頁數4
期刊Journal of the American Ceramic Society
98
發行號4
DOIs
出版狀態已發佈 - 2015 4月

ASJC Scopus subject areas

  • 陶瓷和複合材料
  • 材料化學

指紋

深入研究「Dielectric properties of ultra-low sintering temperature Al2O3-BBSZ glass composite」主題。共同形成了獨特的指紋。

引用此