Developing the properties of polyvinylidene fluoride/(Ba 0.8Sr0.2)(Ti0.9Zr0.1)O3 composite films for embedded capacitors using

Chia Ching Wu*, Tai Ping Sun, Yuan Tai Hsieh, Chin-Guo Kuo, Cheng Fu Yang

*此作品的通信作者

研究成果: 書貢獻/報告類型會議論文篇章

摘要

The average particle sizes of nanoscale (Ba0.8Sr 0.2)(Ti0.9 Zr0.1)O3 ceramic powder (nano-BSTZ) was approximately 73nm. Polyvinylidene fluoride (PVDF)/nano-BSTZ composite films with various contents of the nano-BSTZ were screen-printed on indium tin oxide glass substrates. From the XRD patterns, PVDF was the semicrystalline type polymer. The content of the nano-BSTZ increased from 10 wt% to 50 wt%, the dielectric constants of the PVDF/nano-BSTZ films slightly decreased with increasing measured frequency. The specific capacitance values of the PVDF/nano-BSTZ composite films mixing with 50 wt% nano-BSTZ was 11.6 nF/cm2 (measured at 1 kHz). Those results suggested that the PVDF/nano-BSTZ composite films were a good candidate to develop thinner embedded capacitor devices with higher capacitance value.

原文英語
主出版物標題4th IEEE International NanoElectronics Conference, INEC 2011
DOIs
出版狀態已發佈 - 2011 九月 26
事件4th IEEE International Nanoelectronics Conference, INEC 2011 - Tao-Yuan, 臺灣
持續時間: 2011 六月 212011 六月 24

出版系列

名字Proceedings - International NanoElectronics Conference, INEC
ISSN(列印)2159-3523

其他

其他4th IEEE International Nanoelectronics Conference, INEC 2011
國家/地區臺灣
城市Tao-Yuan
期間2011/06/212011/06/24

ASJC Scopus subject areas

  • 電氣與電子工程

指紋

深入研究「Developing the properties of polyvinylidene fluoride/(Ba <sub>0.8</sub>Sr<sub>0.2</sub>)(Ti<sub>0.9</sub>Zr<sub>0.1</sub>)O<sub>3</sub> composite films for embedded capacitors using」主題。共同形成了獨特的指紋。

引用此