Desorption of surfactant and sintering of surface-modified Pd x Ni 1 - x nanoparticles

Kuan Wen Wang, Shu Ru Chung, Wei Hsiu Hung, Tsong P. Perng*

*此作品的通信作者

研究成果: 雜誌貢獻期刊論文同行評審

6 引文 斯高帕斯(Scopus)

摘要

A series of Pd x Ni 1 - x nanoparticles in a diameter of 6-7 nm were prepared by wet chemical reduction. They were then modified with two surfactants, stearic acid (SA) and polyethylene glycol (PEG). Desorption of the surfactant was studied using a temperature programmed desorption technique, and the sintering behavior of surface-modified Pd x Ni 1 - x nanoparticles was examined. Since surface energy of the nanoparticles depends on the alloy composition, it can be correlated with the desorption temperature of surfactant from the nanoparticle surface. Because Ni has a higher surface energy, the surfactant desorption temperature increases as the Ni content increases. With the same stoichiometry, the desorption temperature of SA is always higher than that of PEG. The SA-modified nanoparticles have higher thermal stability and are less sintered than PEG-modified nanoparticles. The sintering and growth behavior of the nanoparticles can be correlated with variation of surface energy due to different surface modification.

原文英語
頁(從 - 到)8751-8755
頁數5
期刊Applied Surface Science
252
發行號24
DOIs
出版狀態已發佈 - 2006 十月 15

ASJC Scopus subject areas

  • 化學 (全部)
  • 凝聚態物理學
  • 物理與天文學 (全部)
  • 表面和介面
  • 表面、塗料和薄膜

指紋

深入研究「Desorption of surfactant and sintering of surface-modified Pd <sub>x</sub> Ni <sub>1 - x</sub> nanoparticles」主題。共同形成了獨特的指紋。

引用此