Dependence on size of supported Rh nanoclusters for CO adsorption

Ting Chieh Hung, Ting Wei Liao, Zhen He Liao, Po Wei Hsu, Pei Yang Cai, Wen Hua Lu, Jeng Han Wang, Meng Fan Luo

研究成果: 雜誌貢獻文章

7 引文 斯高帕斯(Scopus)

摘要

We studied the adsorption and lateral interactions of CO molecules on Rh nanoclusters supported on an ordered thin film of Al2O3/NiAl(100) with varied surface probe techniques under ultra-high vacuum conditions and with density-functional-theory (DFT) calculations. The Rh clusters were grown with vapor deposition onto the Al2O3/NiAl(100) surface at 300 K; with increasing deposition, their mean diameter evolved from 1.0 to 3.5 nm and their height from 0.4 to 0.8 nm. The initial adsorption energy (for sparse CO coverage) and the number of adsorbed CO per surface site on the Rh clusters increased with decreasing cluster size. The former effect results from the surface structure and expanded lattice parameter of small Rh clusters, whereas the latter effect involves not only the initial adsorption energy but also altered lateral interactions among CO molecules. In contrast with CO on Rh single crystals, CO on small clusters adsorbed with their axes tilted from the surface normal, weakening the CO-CO repulsive interactions for CO coverage over a wide range. The saturated density of CO on clusters of diameter near 1.0 nm and height near 0.4 nm is 2-3 times that of large clusters (diameter ≥ 3.5 nm) or a Rh(100) surface. The CO-CO repulsive interactions on small clusters became effective at large CO densities, given that the onset of desorption of CO at saturation was 100 K lower than that of large clusters.

原文英語
頁(從 - 到)3830-3839
頁數10
期刊RSC Advances
6
發行號5
DOIs
出版狀態已發佈 - 2016 一月 1

ASJC Scopus subject areas

  • Chemistry(all)
  • Chemical Engineering(all)

指紋 深入研究「Dependence on size of supported Rh nanoclusters for CO adsorption」主題。共同形成了獨特的指紋。

  • 引用此

    Hung, T. C., Liao, T. W., Liao, Z. H., Hsu, P. W., Cai, P. Y., Lu, W. H., Wang, J. H., & Luo, M. F. (2016). Dependence on size of supported Rh nanoclusters for CO adsorption. RSC Advances, 6(5), 3830-3839. https://doi.org/10.1039/c5ra20384h