Crystal Structure and Superconductivity of the Mo-Stabilized Sr-Based YSr2Cu2.7Mo0.3O7-δ Compound

S. F. Hu*, R. S. Liu, S. C. Su, D. S. Shy, D. A. Jefferson

*此作品的通信作者

研究成果: 雜誌貢獻編者言同行評審

12 引文 斯高帕斯(Scopus)

摘要

The crystal structure of the Mo-stabilized Sr-based superconductor with nominal composition YSr2Cu2.7Mo0.3O7-δ has been analyzed by X-ray powder diffraction (XRD), electron diffraction, and high-resolution electron microscope techniques. The material crystallizes in the space group P4/mmm, with lattice parameters a = 3.8138(2) and c = 11.5204(8) Å. In the structure, the Mo ions are exclusively substituted for copper and are located mainly on the planar coordinated [Cu(2)] sites (∼24%), with only a small proportion on the chain [Cu(1)] sites (∼6%) in the parent YBa2Cu3O7 (123-type) structure. A disordering of the hole reservoir layer [Mo(1)/Cu(1)]-O(3) due to the displacement of the oxygen ions [O(3)] from their ideal positions of (0, 0.5, 0) to (0.13, 0.5, 0) was found in the XRD refinement, but neither a superlattice nor any form of intergrowth along the a* and c* directions was observed by electron diffraction and high-resolution electron microscopy. The chemical substitution of copper by molybdenum renders the YSr2Cu3O7 compound superconducting, with Tc up to 45 K.

原文英語
頁(從 - 到)203-207
頁數5
期刊Journal of Solid State Chemistry
112
發行號1
DOIs
出版狀態已發佈 - 1994 九月

ASJC Scopus subject areas

  • 電子、光磁材料
  • 陶瓷和複合材料
  • 凝聚態物理學
  • 物理與理論化學
  • 無機化學
  • 材料化學

指紋

深入研究「Crystal Structure and Superconductivity of the Mo-Stabilized Sr-Based YSr<sub>2</sub>Cu<sub>2.7</sub>Mo<sub>0.3</sub>O<sub>7-δ</sub> Compound」主題。共同形成了獨特的指紋。

引用此