Conductivity and dielectric relaxation phenomena in (NH4)2SO4 single crystal

R. H. Chen*, Yu Chao Chen, C. S. Shern, T. Fukami


研究成果: 雜誌貢獻期刊論文同行評審

16 引文 斯高帕斯(Scopus)


AC impedance measurements have been carried out on (NH4)2SO4 single crystals for the temperatures from 300 to 473 K and frequency range between 100 Hz and 4 MHz. The results reveal two distinct relaxation processes in the sample crystal. One is the dipolar relaxation with a peak at frequency slightly higher than 4 × 106 Hz. The other is the charge carrier relaxation at lower frequencies. The frequency dependence of conductivity is described by the relation σ(ω) = Bωn, and n = 1.32 is obtained at temperatures below 413 K. This value drops to 0.2 and then decreases slightly with increasing temperature. The dipolar response of the (NH4)2SO4 single crystal under an ac field is attributed to the reorientation of dipoles. The contribution of charge carriers is increasing substantially with increasing temperature at temperatures above 413 K. The temperature variation of conductivity relaxation peaks follows the Arrhenius relation. The obtained activation energy for migration of the mobile ions for (NH4)2SO4 single crystal was 1.24 eV in the temperature range between 433 and 468 K in this intrinsic region. It is proposed that the NH4+ in the sample crystal has the contribution to the electrical conduction.

頁(從 - 到)356-361
期刊Solid State Ionics
出版狀態已發佈 - 2009 4月 27

ASJC Scopus subject areas

  • 一般化學
  • 一般材料科學
  • 凝聚態物理學


深入研究「Conductivity and dielectric relaxation phenomena in (NH4)2SO4 single crystal」主題。共同形成了獨特的指紋。